Electrical steel sheet and method for manufacturing the same
An electrical steel sheet ( 10 ) is provided with a base iron ( 1 ) and an insulating film ( 2 ) formed on a surface of the base iron ( 1 ). The insulating film ( 2 ) contains: a first component: 100 parts by mass, the first component containing: a metal phosphate: 100 parts by mass; and one kind selected from a group consisting of an acrylic resin, an epoxy resin and a polyester resin which have an average particle size of 0.05 μm to 0.50 μm, or a mixture or copolymer of two or three kinds selected from the group: 1 part by mass to 50 parts by mass; and a second component composed of dispersion or powder of a fluorine resin having an average particle size of 0.05 μm to 0.35 μm: 0.5 parts by mass to 10 parts by mass.
1. A non-oriented electrical steel sheet, comprising:
a base iron; and
an insulating film having a thickness of 0.3 μm to 0.8 μm directly formed on a surface of the base iron;
wherein the insulating film contains:
a first component: 100 parts by mass, the first component containing:
a metal phosphate: 100 parts by mass;
one or more resins selected from the group consisting of an acrylic resin, an epoxy resin and a polyester resin which have an average particle size of 0.05 μm to 0.50 μm in an amount of 1 part by mass to 50 parts by mass; and
a phosphonic acid;
a second component comprising dispersion or powder of a fluorine resin having an average particle size of 0.05 μm to 0.35 μm in an amount of 0.5 parts by mass to 10 parts by mass; and
other component comprising one or more selected from the group consisting of titanate and tungstate;
wherein the fluorine resin is one or more of tetrafluoroethylene-perfluoroalkylvinyl ether copolymer, tetrafluoroethylene-ethylene copolymer, or chlorotrifluoroethylene-ethylene copolymer,
wherein the non-oriented electrical steel sheet has interlayer resistance of 10Ω·cm 2 /piece or more, and
wherein the base iron comprises 0.1-4.0 mass % Si, 0.05-3.0 mass % Al, 0.01-1.0 mass % Mn, 0.01-1.0 mass % Sn, less than 100 ppm S, less than 100 ppm N, less than 100 ppm C, and a balance comprising Fe and inevitable impurities.