Grain-oriented electrical steel sheet and manufacturing method thereof
View Patent ↗A silicon steel sheet ( 1 ) containing Si is cold-rolled. Next, a decarburization annealing ( 3 ) of the silicon steel sheet ( 1 ) is performed so as to cause a primary recrystallization. Next, the silicon steel sheet ( 1 ) is coiled so as to obtain a steel sheet coil ( 31 ). Next, an annealing ( 6 ) of the steel sheet coil ( 31 ) is performed through batch processing so as to cause a secondary recrystallization. Next, the steel sheet coil ( 31 ) is uncoiled and flattened. Between the cold-rolling and the obtaining the steel sheet coil ( 31 ), a laser beam is irradiated a plurality of times at predetermined intervals on a surface of the silicon steel sheet ( 1 ) from one end to the other end of the silicon steel sheet ( 1 ) along a sheet width direction ( 2 ). When the secondary recrystallization is caused, grain boundaries passing from a front surface to a rear surface of the silicon steel sheet ( 1 ) along paths of the laser beams are generated.
1. A manufacturing method of a grain-oriented electrical steel sheet, comprising:
cold-rolling a silicon steel sheet containing Si;
next, performing a decarburization annealing of the silicon steel sheet so as to cause a primary recrystallization;
next, coiling the silicon steel sheet so as to obtain a steel sheet coil;
next, performing an annealing of the steel sheet coil through batch processing so as to cause a secondary recrystallization; and
next, uncoiling and flattening the steel sheet coil, wherein
the manufacturing method further comprising, between the cold-rolling the silicon steel sheet containing Si and the coiling the silicon steel sheet so as to obtain the steel sheet coil, irradiating a laser beam a plurality of times at a predetermined interval in a rolling direction on a surface of the silicon steel sheet from one end to the other end of the silicon steel sheet along a sheet width direction, and
when
an average intensity of the laser beam is P (W),
a size in the rolling direction of a focused beam spot of the laser beam is Dl (mm),
a scanning rate in the sheet width direction of the laser beam is Vc (mm/s), and
an irradiation energy density of the laser beam is Up=4/π×P/(Dl×Vc),
the following relation is satisfied so as to create grain boundaries passing from a front surface to a rear surface of the silicon steel sheet along paths of the laser beams while the secondary recrystallization is caused,
0.5 J/mm 2 ≦Up≦ 20 J/mm 2 .
2. The manufacturing method of a grain-oriented electrical steel sheet according to claim 1 , wherein a part of the surface of the silicon steel sheet to which the laser beam has been irradiated is flat.
3. The manufacturing method of a grain-oriented electrical steel sheet according to claim 1 , wherein the predetermined interval is set based on a radius of curvature of the silicon steel sheet in the steel sheet coil.
4. The manufacturing method of a grain-oriented electrical steel sheet according to claim 1 , wherein, when a radius of curvature at an arbitrary position in the silicon steel sheet in the steel sheet coil is R (mm) and the predetermined interval at the position is PL (mm), the following relation is satisfied,
PL≦ 0.13× R.
5. The manufacturing method of a grain-oriented electrical steel sheet according to claim 4 , wherein the predetermined interval is fixed.
6. The manufacturing method of a grain-oriented electrical steel sheet according to claim 4 , wherein the predetermined interval is wider as the position approaches from an inner surface toward an outer surface of the steel sheet coil.
7. The manufacturing method of a grain-oriented electrical steel sheet according to claim 1 , wherein the predetermined interval is 2 mm or more.
8. The manufacturing method of a grain-oriented electrical steel sheet according to claim 1 , wherein, when
an average intensity of the laser beam is P (W),
a size in the rolling direction and a size in the sheet width direction of a focused beam spot of the laser beam are Dl (mm) and Dc (mm), respectively, and
a local power density of the laser beam is Ip=4/π×P/(Dl×Dc),
the following relation is satisfied,
Ip≦ 100 kW/mm 2 .
9. A grain-oriented electrical steel sheet, comprising
grain boundaries each extending from a front surface to a rear surface of the grain-oriented electrical steel sheet in a thickness direction and from one end to the other end of the grain-oriented electrical steel sheet along a laser scan path in a sheet width direction,
wherein, when an angle between rolling direction of the grain-oriented electrical steel sheet and a direction of an axis of easy magnetization direction <001> of each crystal grain in a sheet thickness direction is defined as β (°), an average value of β at a position separated by 1 mm from the grain boundary in the rolling direction is 7.3° or less.
10. The grain-oriented electrical steel sheet according to claim 9 , wherein a surface of a base material along the grain boundary is flat.