Method for manufacturing an aerogel-containing composite and composite produced by that method
Method for manufacturing an aerogel-containing composite, said method comprising the steps of: providing fibers, at least some of which are first fibers, such as mineral fibers, polymer fibers, cellulose fibers, or other types of fibers, in an amount of from 3 to 80 wt % of the total weight of starting materials, providing an aerogel particulate material in an amount of from 10 to 75 wt % of the total weight of starting materials, providing a binder in an amount of from 1 to 30 wt % of the total weight of starting materials, suspending the fibers in a primary air flow and suspending the aerogel particulate material in the primary air flow, thereby mixing the suspended aerogel particulate material with the suspended fibers, mixing the binder with the fibers and/or aerogel particulate material before, during or after mixing of the fibers with the aerogel particulate material, collecting the mixture of fibers, aerogel particulate material and binder and pressing and curing the mixture to provide a consolidated composite with a density of from 120 kg/m 3 to 800 kg/m 3 . With this method homogeneous composites can be produced.
1. A method for manufacturing an aerogel-containing composite from starting materials having a total weight, said method comprising:
providing fibres, at least some of which are first fibres of a first material in an amount of from 3 to 80 wt % of the total weight of starting materials,
providing an aerogel particulate material in an amount of from 10 to 75 wt % of the total weight of starting materials,
providing a binder in an amount of from 1 to 30 wt % of the total weight of starting materials,
suspending the fibres in a primary air flow and suspending the aerogel particulate material in the primary air flow, thereby mixing the suspended aerogel particulate material with the suspended fibres,
wherein the aerogel particulate material is provided to the primary airflow via a tributary airflow, and wherein the primary airflow is lateral and the tributary airflow is upwards,
mixing the binder with the fibres and/or aerogel particulate material before, during or after mixing of the fibres with the aerogel particulate material, thereby forming a mixture,
collecting the mixture and pressing and curing the mixture to provide a consolidated composite with a density of from 120 kg/m 3 to 800 kg/m 3 .
2. A method according to claim 1 , comprising an intermediate step of providing second fibres of a second material different from the first material of the first fibres in an amount of 3 to 80 wt % of the total weight of starting materials.
3. A method according to claim 1 , wherein the first fibres are mineral fibres.
4. A method according to claim 2 , wherein the second fibres are polymer fibres.
5. A method according to claim 1 , wherein the step of mixing binder with the fibres is performed before suspending the fibres in the primary air flow.
6. A method according to claim 1 , wherein the first fibres are stone wool fibres.
7. A method according to claim 1 , wherein the step of mixing binder with the fibres is performed at production of the fibres.