Process for producing highly conducting and transparent films from graphene oxide-metal nanowire hybrid materials
View Patent ↗A process for producing a transparent conductive film, comprising (a) providing a graphene oxide gel; (b) dispersing metal nanowires in the graphene oxide gel to form a suspension; (c) dispensing and depositing the suspension onto a substrate; and (d) removing the liquid medium to form the film. The film is composed of metal nanowires and graphene oxide with a metal nanowire-to-graphene oxide weight ratio from 1/99 to 99/1, wherein the metal nanowires contain no surface-borne metal oxide or metal compound and the film exhibits an optical transparence no less than 80% and sheet resistance no higher than 300 ohm/square. This film can be used as a transparent conductive electrode in an electro-optic device, such as a photovoltaic or solar cell, light-emitting diode, photo-detector, touch screen, electro-wetting display, liquid crystal display, plasma display, LED display, a TV screen, a computer screen, or a mobile phone screen.
1. A process for producing an optically transparent and electrically conductive film, said process consisting essentially of (a) providing a graphene oxide gel prepared from oxidation of a graphitic material in an oxidizing medium wherein said graphene oxide gel contains graphene oxide molecules dissolved in a liquid medium; (b) dispersing metal nanowires in said graphene oxide gel to form a suspension; (c) dispensing and depositing said suspension onto a supporting substrate; and (d) removing said liquid medium from said suspension to form said optically transparent and electrically conductive film, which consists of metal nanowires and graphene oxide having a metal nanowire-to-graphene oxide weight ratio of from 1/99 to 99/1, wherein said metal nanowires contain no surface-borne metal oxide or metal compound and said film exhibits an optical transparence no less than 80% and sheet resistance no higher than 300 ohm/square.
2. The process of claim 1 , further comprising a step of thermally and/or chemically reducing said graphene oxide to a reduced graphene oxide having an oxygen content no greater than 2% by weight.
3. The process of claim 1 , wherein said metal nanowires are selected from nanowires of silver (Ag), gold (Au), copper (Cu), platinum (Pt), zinc (Zn), cadmium (Cd), cobalt (Co), molybdenum (Mo), aluminum (Al), an alloy thereof, or a combination thereof.
4. The process of claim 1 , wherein said metal nanowires contain silver nanowires.
5. The process of claim 1 , wherein said metal nanowires contain copper nanowires.
6. The process of claim 1 , wherein said metal nanowires are selected from nanowires of a transition metal or an alloy of a transition metal.
7. The process of claim 1 , wherein said graphene oxide contains single-layer graphene or few-layer graphene having less than 10 graphene planes of atoms.
8. The process of claim 1 , wherein said graphene oxide gel is composed of graphene oxide molecules dispersed in an acidic medium having a pH value of no higher than 5 and said graphene oxide molecules have an oxygen content no less than 20% by weight while in a gel state.
9. The process of claim 1 , wherein said graphene oxide gel is obtained by immersing a graphitic material in a powder or fibrous form in an oxidizing liquid medium in a reaction vessel at a reaction temperature for a length of time sufficient to obtain a graphene oxide gel composed of graphene oxide molecules dispersed in the liquid medium and said graphene oxide molecules have an oxygen content no less than 20% by weight and a molecular weight less than 43,000 g/mole while in a gel state.
10. The process of claim 1 , wherein said graphene oxide molecules have a molecular weight less than 4,000 g/mole while in a gel state.
11. The process of claim 1 , wherein said graphene oxide molecules have a molecular weight between 200 g/mole and 4,000 g/mole while in a gel state.
12. The process of claim 1 , wherein step (c) of dispensing and depositing contains a coating or casting procedure.
13. The process of claim 1 , wherein step (c) of dispensing and depositing contains a procedure selected from spray painting, drop casting, spin coating, vacuum-assisted filtration, electrostatic deposition, or dip coating.
14. The process of claim 1 , wherein said film exhibits an optical transparence no less than 85% and sheet resistance no higher than 100 ohm/square.
15. The process of claim 1 , wherein said film exhibits an optical transparence no less than 85% and sheet resistance no higher than 50 ohm/square.
16. The process of claim 1 , wherein said film exhibits an optical transparence no less than 90% and sheet resistance no higher than 200 ohm/square.
17. The process of claim 1 , wherein said film exhibits an optical transparence no less than 90% and sheet resistance no higher than 100 ohm/square.
18. The process of claim 1 , wherein said film exhibits an optical transparence no less than 95% and sheet resistance no higher than 100 ohm/square.
19. The process of claim 1 , wherein said supporting substrate is optically transparent.
20. The process of claim 1 , wherein said suspension further contains carbon nanotubes or carbon nano-fibers.
21. The process of claim 1 , wherein said supporting substrate is moved from a feeder roller to a collector roller and the process contains a roll-to-roll procedure.