Grain-oriented electrical steel sheet and method of manufacturing the same
View Patent ↗This method of manufacturing a grain-oriented electrical steel sheet includes, between a cold rolling process and a winding process, a groove formation process of irradiating the surface of a silicon steel sheet with a laser beam multiple times at predetermined intervals in a sheet passing direction, over an area from one end edge to the other end edge, in a sheet width direction of the silicon steel sheet, thereby forming a groove along a locus of the laser beam.
1. A grain-oriented electrical steel sheet comprising:
a groove formed from a locus of a laser beam scanned over an area from one end edge to the other end edge in a sheet width direction; and
a crystal grain boundary which extends along the groove and penetrates the grain-oriented electrical steel sheet from a front surface to a back surface, wherein
a glass coating is formed in the groove,
wherein in the glass coating, an X-ray intensity ratio (Ir) of a characteristic X-ray intensity of Mg at a portion of the groove is in a range of 0≦Ir≦0.9,
and wherein an average value of the characteristic X-ray intensity of Mg of portions other than the portion of the groove of the surface of the grain-oriented electrical steel sheet is set to be 1.
2. The grain-oriented electrical steel sheet according to claim 1 , further comprising a crystal grain in which a grain diameter thereof in the sheet width direction of the grain-oriented electrical steel sheet is greater than or equal to 10 mm and less than or equal to a sheet width and a grain diameter thereof in a longitudinal direction of the grain-oriented electrical steel sheet exceeds 0 mm and is 10 mm or less,
wherein the crystal grain is present to over a range from the groove to the back surface of the grain-oriented electrical steel sheet.