Continuous digital light processing additive manufacturing of implants
A process for additive manufacturing of a resorbable implant to be implanted into a patient includes providing a biocompatible resin including a liquid light-polymerizable material that is resorbable after polymerization and an initiator. The process further includes actuating an additive manufacturing apparatus to expose an amount of the biocompatible resin to light to at least partially cure the exposed amount of biocompatible resin to form a layer of the resorbable implant and actuating the additive manufacturing apparatus to expose at least some additional amount of biocompatible resin to light to at least partially cure the exposed additional amount of biocompatible resin to form an additional layer of the resorbable implant and to at least partially overcure previously cured layers to cause at least some interlayer binding between the previously cured layers and the additional layer.
1. A method of manufacturing a tissue engineering scaffold for implantation in a patient and promoting tissue growth, the method comprising:
receiving data representing at least the tissue engineering scaffold at a Digital Light Processing (DLP) additive manufacturing apparatus including a Digital Micromirror Device (DMD);
actuating the DMD to project light corresponding to layers of the scaffold onto a transparent or translucent plate above which is disposed a build plate and a biocompatible resin including a liquid light-polymerizable material that is resorbable after polymerization, wherein the resin includes a dye and an initiator;
shifting the build plate at selected increments such that the projected light sequentially causes portions of the resin to at least partially polymerize to substantially resemble the layers of the scaffold; and
controlling depth of penetration of the projected light by selecting the ratio of the dye to the initiator in the biocompatible resin so that the projected light overcures a previously at least partially polymerized layer,
wherein the ratio of dye to initiator is selected to control light penetration such that overcuring of at least one previously rendered layer is in a range between 10% and 300% of layer thickness.
2. The method of claim 1 , wherein the produced scaffold includes pores having openings with diameters in the range of 50 to 1600 micrometers.
3. The method of claim 1 , wherein the polymerization produces the scaffold to include pores that are oblique.
4. The method of claim 1 , wherein the polymerization produces the scaffold to have at least one surface that has formed thereon indentations and protrusions having diameters ranging from 1 nanometer to 100 micrometers.
5. The method of claim 1 , wherein the polymerization produces the scaffold to include at least one surface that has at least one of indentations and protrusions having diameters ranging from 1 nanometer to 100 micrometers.
6. The method of claim 1 , wherein the liquid light-polymerizable material has a molecular weight of approximately 4,000 Daltons or less.
7. The method of claim 1 , wherein the liquid light-polymerizable material has a molecular weight of approximately 1,200 Daltons or less.
8. The method of claim 1 , wherein the liquid light-polymerizable material is poly(propylene fumarate) (PPF).
9. The method of claim 1 , wherein the resin includes at least one of a bioactive compound and an antibiotic.
10. The method of claim 1 , wherein the actuating the DMD to project light simultaneously projects all pixels in an entire voxel data set representing a complete layer of the scaffold.
11. The method of claim 10 , wherein the actuating the DMD to project light simultaneously projects at least a first pixel at a different intensity or irradiance than a second pixel.
12. The method of claim 1 , wherein the actuating the DMD to project light projects pixels having at least one dimension of 75 micrometers or less.
13. The method of claim 1 , wherein the shifting the build plate at selected increments elevates the build plate at increments of 50 micrometers or less.
14. The method of claim 1 , wherein the ratio of dye to initiator is selected to control light penetration such that overcuring of at least one previously rendered layer is in at least one of a range between 10% and 50% and a range between 40% and 100% of layer thickness.
15. The method of claim 1 , wherein the actuating the DMD to project light includes projecting light at an elevated level of irradiance to increase scaffold green strength.
16. The method of claim 1 , wherein the initiator is bis(2,4,6-trimethylbenzoyl)phenylphosphine oxide (BAPO).
17. The method of claim 1 , wherein the dye is titanium dioxide (TiO2).
18. The method of claim 1 , wherein the resin further includes a solvent.
19. The method of claim 1 , wherein the resin further includes diethyl fumarate (DEF).