View Patent ↗There is provided a steel for induction hardening in which cracks are less liable to occur and high hardness and seizure resistance are attained even if a tempering process after induction hardening is omitted. The steel for induction hardening according to the present invention contains, by mass percent, C: 0.20 to 0.34%, Si: at most 0.20%, Mn: 0.75 to 2.0%, P: at most 0.03%, S: at most 0.20%, Cr: 0.05 to 1.2%, Ti: at least 0.002% and less than 0.030%, Al: 0.005 to 0.04%, and N: 0.0040 to 0.020%, the balance being Fe and impurities, and satisfies Formula (1): 1.20≦Mn+Cr≦2.10 (1) where the content (mass %) of each element is substituted for each of the symbols of elements in Formula (1).
1. A crankshaft comprising an induction hardened and hot forged steel, containing, by mass percent, C: 0.20 to 0.34%, Si: at most 0.20%, Mn: 0.75 to 2.0%, P: at most 0.03%, S: at most 0.20%, Cr: 0.05 to 1.2%, Ti: at least 0.002% and less than 0.030%, Al: 0.014 to 0.04%, and N: 0.0040 to 0.020%, the balance being Fe and impurities, and satisfying Formula (1):
1.20≦Mn+Cr≦2.10 (1)
where the content (mass %) of each element is substituted for each of the symbols of elements in Formula (1).
2. The crankshaft according to claim 1 , which is manufactured by being not tempered.