Methods for producing iron methacrylate and hydroxyalkyl methacrylate
View Patent ↗There is provided a method for producing iron methacrylate being inexpensive, and being high in activity and selectivity and good in solubility to a reaction liquid when being used in production of a hydroxyalkyl methacrylate as a catalyst. The method for producing iron methacrylate for production of a hydroxyalkyl methacrylate according to the present invention includes subjecting a mixture of a metallic iron having an oxygen atom content by XRF analysis of the surface thereof of 6% by mass or lower, and methacrylic acid to a heat treatment at 95° C. or higher and lower than 110° C. for 100 to 600 min. The method for producing a hydroxyalkyl methacrylate according to the present invention includes reacting an alkylene oxide with methacrylic acid to produce the hydroxyalkyl methacrylate, wherein iron methacrylate produced by the method according to the present invention is used as a catalyst.
1. A method for producing iron methacrylate, the method comprising subjecting a mixture of a metallic iron and methacrylic acid to a heat treatment at a temperature of from 95° C. to 110° C. for 100 to 600 min,
wherein the metallic iron has an oxygen atom content by XRF analysis of a surface thereof of 6% by mass or lower.
2. The method of claim 1 , further comprising:
subjecting the mixture, after the heat treatment, to a further heat treatment at a temperature of from 110° C. to 125° C. for 30 to 300 min, and
subsequently cooling to 100° C. or lower.
3. A method for producing a hydroxyalkyl methacrylate the method comprising reacting an alkylene oxide with a methacrylic acid and the iron methacrylate of claim 1 ,
wherein the iron methacrylate is a catalyst.
4. The method of claim 3 , further comprising reacting with a quaternary ammonium salt and an amine compound,
wherein the quaternary ammonium salt and amine compound are catalysts.
5. The method of claim 4 , wherein the quaternary ammonium salt is in an amount of from 0.5 to 1.5 mol with respect to 1 mol of the iron methacrylate.
6. A method for producing a hydroxyalkyl methacrylate, the method comprising reacting an alkylene oxide with a methacrylic acid and the iron methacrylate of claim 2 ,
wherein the iron methacrylate is a catalyst.
7. The method of claim 6 , further comprising reacting with a quaternary ammonium salt and an amine compound,
wherein the quaternary ammonium salt and amine compound are catalysts.
8. The method of claim 7 , wherein the quaternary ammonium salt is in an amount of from 0.5 to 1.5 mol with respect to 1 mol of the iron methacrylate.
9. The method of claim 1 , wherein the metallic iron is an iron powder.
10. The method of claim 9 , wherein a particle diameter of the iron powder is of from 10 to 500 μm.
11. The method of claim 9 , wherein a particle diameter of the iron powder is of from 60 to 300 μm.
12. The method of claim 1 , wherein the metallic iron has an oxygen atom content by XRF analysis of a surface thereof of 3% by mass or lower.
13. The method of claim 1 , wherein the metallic iron has an oxygen atom content by XRF analysis of a surface thereof is of from 0% to 6% by mass.
14. The method of claim 1 , wherein the metallic iron has an oxygen atom content by XRF analysis of a surface thereof is of from 1% to 6% by mass.
15. The method of claim 1 , wherein the metallic iron has an oxygen atom content by XRF analysis of a surface thereof is of from 1.5% to 6% by mass.
16. The method of claim 1 , wherein the heat treatment is at a temperature of from 95° C. to 105° C.
17. The method of claim 1 , wherein the heat treatment is carried out for 150 to 500 min.
18. The method of claim 1 , wherein the heat treatment is carried out for 200 to 400 min.
19. The method of claim 1 , wherein an amount of moisture of the methacrylic acid is 300 ppm or smaller.
20. The method of claim 1 , wherein an amount of moisture of the methacrylic acid is 200 ppm or smaller.