Rubber composition for tires and pneumatic tire
View Patent ↗A rubber composition for tires contains a diene rubber, silica, a sulfur-containing silane coupling agent and a triethoxysilane containing an alkyl group having a prescribed number of carbon atoms, wherein 50 mass % or more of the aforementioned diene rubber is a styrene-butadiene copolymer rubber, the aforementioned sulfur-containing silane coupling agent has a mercapto group, the content of the aforementioned silica is from 5 to 150 parts by mass per 100 parts by mass of the aforementioned diene rubber, the content of the aforementioned sulfur-containing silane coupling agent is from 3 to 15 mass % relative to the content of the aforementioned silica, and the content of the aforementioned alkyltriethoxysilane is from 0.1 to 20 mass % relative to the content of the aforementioned silica.
1. A rubber composition for tires, consisting of a diene rubber, non-aggegated silica, a sulfur-containing silane coupling agent and an alkyltriethoxysilane represented by formula (I) below, wherein
50 mass % or more of the diene rubber is a styrene-butadiene copolymer rubber,
the sulfur-containing silane coupling agent has a mercapto group,
the content of the silica is from 5 to 150 parts by mass per 100 parts by mass of the diene rubber,
the content of the sulfur-containing silane coupling agent is from 3 to 15 mass % relative to the content of the silica, and
the content of the alkyltriethoxysilane is from 0.1 to 20 mass % relative to the content of the silica and has the formula;
in the formula, R 1 is an alkyl group having 7 to 20 carbon atoms, and
wherein the silica has a CTAB adsorbtion specific surface area of greater than 160 m 2 /g,
and
additives selected from the group consisting of fillers excluding aggregated silica, crosslinking agents, crosslinking accelerators, zinc oxide, oils, anti-aging agents, plasticizers and mixtures thereof.
2. The rubber composition for tires according to claim 1 , wherein a weight-average molecular weight of the styrene-butadiene rubber is from 900,000 to 2,000,000.
3. A pneumatic tire that uses the rubber composition according to claim 1 .
4. A pneumatic tire that uses the rubber composition according to claim 2 .
5. The rubber composition for tires according to claim 1 , wherein the styrene-butadiene rubber contains from 30 to 50 mass % of an aromatic vinyl and has a vinyl bond content in a conjugated diene of from 30 to 65 mass %.
6. The rubber composition for tires according to claim 1 , wherein the alkyl group having 7 to 20 carbon atoms is an octyl group or a nonyl group.
7. A pneumatic tire that uses the rubber composition according to claim 5 .
8. A pneumatic tire that uses the rubber composition according to claim 6 .
9. A rubber composition for tires according to claim 1 wherein
60 mass % or more of the diene rubber is a styrene-butadiene copolymer rubber,
the content of the silica is from 70 to 100 parts by mass per 100 parts by mass of the diene rubber,
the content of the sulfur containing silane coupling agent is from 5 to 10 mass % relative to the content of the silica, and
the content of the alkyltriethoxysilane is from 0.5 to 10 mass % relative to the content of the silica.