Flame retardant fibers, yarns, and fabrics made therefrom
Disclosed are technical fibers and yarns made with partially aromatic polyamides and non-halogenated flame retardant additives. Fabrics made from such fibers and yarns demonstrate superior flame retardancy over traditional flame retardant nylon 6,6 fabrics. Further, the disclosed fibers and yarns, when blended with other flame retardant fibers, do not demonstrate the dangerous “scaffolding effect” common with flame retardant nylon 6,6 blended fabrics.
1. A flame retardant staple spun yarn comprising at least one flame retardant fiber comprising MXD6 compounded or dispersed with a non-halogen flame retardant additive prior to or during fiber extrusion, wherein the non-halogen flame retardant additives are present at a concentration of from about 5% to about 20% by weight of said fiber and are selected from the group consisting of melamine polyphosphate (MPP), zinc diethylphosphinate (DEPZn), aluminum diethylphosphinate (DEPAI), silicotungstic acid (SiTA), melamine cyanurate (MC) and combinations thereof; said fiber having fabric properties of wear-resistance and durability when formed into a fabric, batting or garment, is self extinguishing in a vertical flammability test ASTM D6413; and
an additional fiber.
2. The flame retardant staple spun yarn of claim 1 , wherein said additional fiber is selected from the group consisting of: cellulose, aramids, phenolic, polyester, oxidized acrylic, modacrylic, melamine, silk, flax, hemp, wool, poly(p-phenylene benzobisoxazole) (PBO), polybenzimidazole (PBI), andpolysulphonamide (PSA) fibers.
3. The flame retardant staple spun yarn of claim 1 , wherein said additional fiber has been treated with a flame retardant.
4. The flame retardant staple spun yarn of claim 1 , wherein said additional fiber is cotton, rayon, polyester, or lyocell.
5. A flame retardant continuous filament yam comprising at least one flame retardant fiber comprising MXD6 compounded or dispersed with a non-halogen flame retardant additive prior to or during fiber extrusion, wherein the non-halogen flame retardant additives are present at a concentration of from about 5% to about 20% by weight of said fiber and are selected from the group consisting of melamine polyphosphate (MPP), zinc diethylphosphinate (DEPZn), aluminum diethylphosphinate (DEPAI), silicotungstic acid (SiTA), melamine cyanurate (MC) and combinations thereof; said fiber having fabric properties of wear-resistance and durability when formed into a fabric, batting or garment, is self extinguishing in a vertical flammability test ASTM D6413, wherein said flame retardant fiber is continuous; and
an additional continuous filament fiber.
6. The flame retardant continuous filament yarn of claim 5 , wherein said additional continuous filament fiber is selected from the group consisting of: aramids, phenolic, polyesters, oxidized acrylic, modacrylic, melamine, lyocell, poly(p-phenylene benzobisoxazole) (PBO), polybenzimidazole (PBI), and polysulphonamide (PSA) fibers.
7. The flame retardant continuous filament yarn of claim 5 wherein said additional continuous filament fiber has been treated with a flame retardant.
8. A fabric comprising the yarn of claim 1 or claim 5 .
9. The fabric of claim 8 further comprising an additional yarn.
10. The fabric of claim 9 , wherein said additional yarn comprises a fiber selected from the group consisting of: cellulose, aramids, phenolic, polyester, oxidized acrylic, modacrylic, melamine, cotton, silk, flax, hemp, wool, rayon, lyocell, poly(p-phenylene benzobisoxazole) (PBO), polybenzimidazole (PBI), and polysulphonamide (PSA) fibers.
11. A nonwoven flame retardant fabric comprising the yarn of claim 1 or claim 5 .
12. The nonwoven flame retardant fabric of claim 11 , wherein said nonwoven is made by a process selected from the group consisting of: spun-bond, melt-blown and a combination thereof.
13. Protective clothing comprising yarn of claim 1 or claim 5 .