Hot rolled thin cast strip product and method for making the same
A hot rolled steel strip made by the steps including assembling a twin roll caster, forming a casting pool of molten steel of such composition that the cast strip produced comprises by weight, greater than 0.25% and up to 1.1% carbon, between 0.40 and 2.0% manganese, between 0.05 and 0.50% silicon, less than 0.01% aluminum, counter rotating the casting rolls to solidify metal shells and forming a steel strip, hot rolling the steel strip such that mechanical properties at 10% and 35% reduction are within 10% for yield strength, tensile strength and total elongation, and coiling the hot rolled steel strip at a temperature between 550 and 750° C. to provide a majority of the microstructure comprising pearlite, along with bainite and acicular ferrite. The steel may have a free oxygen content between 5 and 50 ppm or between 25 and 45 ppm.
1. A hot rolled steel strip made by the steps comprising:
assembling an internally cooled roll caster having laterally positioned casting rolls forming a nip between them, and forming a casting pool of molten steel supported on the casting rolls above the nip and confined adjacent the ends of the casting rolls by side dams, the molten steel of such composition that hot rolled thin cast strip produced has a composition comprising by weight, greater than 0.25% and up to 1.1% carbon, between 0.5 and 2.0% manganese, between 0.05 and 0.50% silicon, less than 0.01% aluminum,
counter rotating the casting rolls to solidify metal shells on the casting rolls as the casting rolls move through the casting pool, and
forming from the metal shells downwardly through the nip between the casting rolls a steel strip,
hot rolling the steel strip such that mechanical properties at 10% and 35% reduction are within 10% for yield strength, tensile strength and total elongation; and
coiling the hot rolled steel strip at a temperature between 550 and 750° C. to provide a majority of the microstructure comprising pearlite, along with bainite and acicular ferrite in the microstructure.
2. The hot rolled steel strip as claimed in claim 1 , the hot rolled steel strip such that mechanical properties at 15% and 35% reduction are within 10% for yield strength, tensile strength and total elongation.
3. The hot rolled steel strip as claimed in claim 1 , the molten steel having a free oxygen content between 5 and 50 ppm.
4. The hot rolled steel strip as claimed in claim 1 , the molten steel having a free oxygen content between 25 and 45 ppm.
5. The hot rolled steel strip as claimed in claim 1 where the steel strip has a thickness of less than 2.5 mm.
6. The hot rolled steel strip as claimed in claim 1 , the molten steel having a composition such that the manganese content of the composition of the hot rolled steel strip is between 0.6 and 1.0% by weight.
7. The hot rolled steel strip as claimed in claim 1 , the molten steel having a composition such that a niobium content of the composition of the hot rolled steel strip is between about 0.01% and 0.2%.
8. The hot rolled steel strip as claimed in claim 1 , the composition further comprising at least one element selected from the group consisting of molybdenum between about 0.05% and about 0.50%, vanadium between about 0.01% and about 0.20%, and a mixture thereof.
9. The hot rolled steel strip as claimed in claim 1 made by the steps further comprising the step of:
hot dip coating the hot rolled steel strip to provide a coating of zinc or a zinc alloy.
10. The hot rolled steel strip as claimed in claim 1 having a tensile strength of at least 800 MPa after hot rolling reductions of 15% and 35%.
11. A hot rolled steel strip made by the steps comprising:
assembling an internally cooled roll caster having laterally positioned casting rolls forming a nip between them, and forming a casting pool of molten steel supported on the casting rolls above the nip and confined adjacent the ends of the casting rolls by side dams, the molten steel of such composition that hot rolled thin cast strip produced has a composition comprising by weight, greater than 0.25% and up to 1.1% carbon, between 0.5 and 2.0% manganese, between 0.05 and 0.50% silicon, less than 0.01% aluminum,
counter rotating the casting rolls to solidify metal shells on the casting rolls as the casting rolls move through the casting pool, and
forming from the metal shells downwardly through the nip between the casting rolls a steel strip,
hot rolling the steel strip such that mechanical properties at 10% and 35% reduction are within 10% for yield strength, tensile strength and total elongation; and
coiling the hot rolled steel strip at a temperature between 200 and 550° C. to provide a majority of the microstructure comprising bainite, martensite, and acicular ferrite, and having less than 5% polygonal ferrite by volume in the microstructure.
12. The hot rolled steel strip as claimed in claim 11 , the hot rolled steel strip such that mechanical properties at 15% and 35% reduction are within 10% for yield strength, tensile strength and total elongation.
13. The hot rolled steel strip as claimed in claim 11 , the molten steel having a free oxygen content between 5 and 50 ppm.
14. The hot rolled steel strip as claimed in claim 11 , the molten steel having a free oxygen content between 25 and 45 ppm.
15. The hot rolled steel strip as claimed in claim 11 where the steel strip has a thickness of less than 2.5 mm.
16. The hot rolled steel strip as claimed in claim 11 , the molten steel having a composition such that the manganese content of the composition of the hot rolled steel strip is between 0.6 and 1.0% by weight.
17. The hot rolled steel strip as claimed in claim 11 , the molten steel having a composition such that a niobium content of the composition of the hot rolled steel strip is between about 0.01% and 0.2%.
18. The hot rolled steel strip as claimed in claim 11 , the composition further comprising at least one element selected from the group consisting of molybdenum between about 0.05% and about 0.50%, vanadium between about 0.01% and about 0.20%, and a mixture thereof.
19. The hot rolled steel strip as claimed in claim 11 made by the steps further comprising the step of:
hot dip coating the hot rolled steel strip to provide a coating of zinc or a zinc alloy.
20. The hot rolled steel strip as claimed in claim 11 having a tensile strength of at least 800 MPa after hot rolling reductions of 15% and 35%.
21. The hot rolled steel strip as claimed in claim 11 having a tensile strength between about 1100 and 1400 MPa after hot rolling reductions of 15% and 35%.
22. The hot rolled steel strip as claimed in claim 11 having a tensile strength between about 1400 and 1700 MPa after hot rolling reductions of 15% and 35%.