Coating system having long-term durability and chemical resistance
View Patent ↗A highly durable coating composition particularly suited for use on printed articles requiring protection from exposure to the natural elements, chemical exposure, or abrasion. The coating composition generally comprises a fluoropolymer resin, an acrylic polyol resin and a melamine resin. Optionally, a polyisocyanate crosslinking agent may also be included to accelerate curing of the coating.
1. A water-based coating composition that, upon curing, forms a highly durable coating, said coating composition comprising:
an acrylic polyol resin;
a fluoropolymer resin;
a melamine resin; and
optionally, a water-dispersible polyisocyanate crosslinking agent.
2. The coating composition according to claim 1 , wherein said fluoropolymer resin comprises alternating fluoroethylene and alkyl vinyl ether segments.
3. The coating composition according to claim 1 , wherein said melamine resin is a methylated melamine resin.
4. The coating composition according to claim 1 , wherein said composition comprises said water-dispersible polyisocyanate.
5. The coating composition according to claim 4 , wherein said polyisocyanate crosslinking agent is based upon hexamethylene diisocyanate.
6. The coating composition according to claim 1 , wherein said composition further comprises an ester alcohol coalescing agent.
7. The coating composition according to claim 6 , wherein said ester alcohol coalescing agent comprises 2,2,4-trimethyl-1,3-pentanediol monoisobutyrate.
8. The coating composition according to claim 1 , wherein said composition further comprises a nonionic fluorosurfactant.
9. The coating composition according to claim 1 , wherein said composition is an un-pigmented clear-coat composition.
10. A water-based coating composition that, upon curing, forms a highly durable coating, said coating composition comprising:
between about 10% to about 40% by weight of one or more acrylic resins;
between about 10% to about 40% by weight of one or more fluoropolymer resins;
between about 3% to about 15% by weight of one or more melamine resins; and
between about 2% to about 10% by weight of an water-dispersible isocyanate crosslinking agent.
11. The composition according to claim 10 , wherein said composition further comprises between about 2% to about 12% by weight of an ester alcohol coalescing agent.
12. The composition according to claim 10 , wherein said composition further comprises between about 0.1 to about 1.5% by weight of a nonionic fluorosurfactant.
13. The composition according to claim 10 , wherein said one or more fluoropolymer resins comprises alternating fluoroethylene and alkyl vinyl ether segments.
14. A method of protecting an image printed upon a substrate comprising:
providing a substrate having an ink image printed thereon;
applying a clear top coat composition to said substrate over at least a portion of said ink image, said clear top coat composition comprising an acrylic polyol resin, a fluoropolymer resin, a melamine resin, and optionally, a water-dispersible polyisocyanate; and
curing said clear top coat composition on said substrate to form a protective coating thereon.
15. The method according to claim 14 , wherein said substrate comprises a primer coating that was applied thereto prior to printing of said ink image thereon.
16. The method according to claim 15 , wherein said primer coating comprises a waterborne acrylic resin.
17. The method according to claim 14 , wherein said substrate is embossed after printing of said ink image thereon.
18. The method according to claim 14 , wherein said clear top coat composition is applied to said substrate by roller coating, screen printing, spraying, or digital printing.
19. The method according to claim 18 , wherein said clear top coat composition comprises said water-dispersible polyisocyanate and is applied to said substrate through a digital printing operation.
20. The method according to claim 19 , wherein said digital printing operation comprises a dual-head inkjet printing system in which said water-dispersible polyisocyanate is discharged toward said substrate from a separate printer head than said acrylic polyol resin, said fluoropolymer resin, and said melamine resin, and thus does not come into contact with said acrylic polyol resin, said fluoropolymer resin, and said melamine resin until discharged.
21. The method according to claim 18 , wherein said clear top coat composition comprises said water-dispersible polyisocyanate, which is mixed with said acrylic polyol resin, said fluoropolymer resin, and said melamine resin no earlier than 8 hours prior to application of said clear top coat composition to said substrate.
22. The method according to claim 14 , wherein said curing step comprises passing said substrate including said clear top coat composition through forced air drying apparatus.
23. The method according to claim 22 , wherein said clear top coat composition does not include said water-dispersible polyisocyanate.
24. The method according to claim 14 , wherein said curing step comprises baking said substrate including said clear top coat composition at a temperature of at least 150° F. for at least 30 seconds.
25. The method according to claim 14 , wherein said clear top coat composition comprises said water-dispersible polyisocyanate, and said curing step comprises allowing said substrate including said clear top coat composition to dry at ambient temperature conditions without application of heat.
26. The method according to claim 14 , wherein said substrate comprises a member selected from the group consisting of ceramic, stainless steel, melamine laminate sheet material, tin, cold rolled steel, polycarbonate, polypropylene, polyethylene, acrylic sheeting, and glass.