Glass plate for display device, plate glass for display device and production process thereof
View Patent ↗A process for producing a plate glass for a display device having a thickness of at most 1.5 mm by a float process, wherein the plate glass comprises, as represented by mole percentage based on the following oxides, from 67 to 75% of SiO2, from 0 to 4% of Al2O3, from 7 to 15% of Na2O, from 1 to 9% of K2O, from 6 to 14% of MgO and from 0 to 1.5% of ZrO2, has a total content of SiO2 and Al2O3 of from 71 to 75%, has a total content Na2O+K2O of Na2O and K2O of from 12 to 20%, and has a content of CaO of less than 1% if contained.
1. A display device, comprising:
a display, and
a cover glass,
wherein the cover glass has a thickness of at most 1 mm;
the cover glass comprises, by mole percentage based on the following oxides:
from 67 to 75% of SiO 2 ,
from 0 to 4% of Al 2 O 3 ,
from 7 to 15% of Na 2 O,
from 1 to 9% of K 2 O,
from 6 to 14% of MgO, and
from 0 to 0.7% of ZrO 2 ,
a total content of SiO 2 and Al 2 O 3 in the cover glass is from 71 to 75%;
a total content Na 2 O+K 2 O of Na 2 O and K 2 O in the cover glass is from 12 to 20%; and
a content in the cover glass of CaO, if present, is less than 1%.
2. The display device according to claim 1 , wherein a SiO 2 content of the cover glass is from 69 to 74 mol %.
3. The display device according to claim 1 , wherein an Al 2 O 3 content of the cover glass is at least 0 mol % and less than 3 mol %.
4. The display device according to claim 1 , wherein a MgO content of the cover glass is from 8 to 13 mol %.
5. The display device according to claim 1 , wherein the total content Na 2 O+K 2 O of the cover glass is higher than 13.5%.
6. The display device according to claim 1 ,
wherein the cover glass comprises CaO, SrO, BaO, ZrO 2 , or any combination thereof, and
a total content of CaO, SrO, BaO, and ZrO 2 is less than 1.5%.
7. The display device according to claim 1 , wherein a content in the cover glass of B 2 O 3 , if present, is less than 1%.
8. The display device according to claim 1 , wherein a temperature at which a viscosity of the cover glass is 10 2 dPa·s is at most 1,650° C.
9. The display device according to claim 1 , wherein an average Linear expansion coefficient of the cover glass at from 50 to 350° C. is higher than 86×10 −7 /° C.
10. The display device according to claim 1 , wherein the display device is a mobile device.
11. The display device according to claim 1 , wherein the display device is a touch panel.
12. The display device according to claim 1 , wherein the thickness Of the cover glass is from 0.2 mm to 1 mm.
13. The display device according to claim 1 , wherein a temperature at which a viscosity of the cover glass is 10 4 dPa·s is at most 1,190° C.
14. The display device according to claim 1 , wherein a Li 2 O content if present in the cover glass is at most 0.05%.