Additive containing N-(N-butyl)thiophosphoric triamide for urea-based fertilizer
A dry flowable additive for aqueous urea-based fertilizers made of solid urea formaldehyde polymer (UFP), N-(n-butyl)thiophosphoric triamide (NBPT), and, optionally, dicyandiamide (DCD), wherein the liquid fertilizer containing the additive provides reduced nitrogen loss from the soil. Optionally, the dry additive may also be blended with molten or solid urea to form a solid urea-based fertilizer with reduced nitrogen loss from the soil.
1. A composition comprising:
a. NBPT in the range of about 1 to about 80 weight %, and
b. solid UFP in the range of about 99 to about 20 weight % wherein the UFP is a polymethyl urea resin, and the UFP is coated with the NBPT.
2. The composition of claim 1 wherein the composition further comprises dicyandiamide (DCD).
3. A composition comprising:
a. NBPT in the range of about 0.40 to about 15 weight %; and
b. Dicyandiamide in the range of about 40 to about 95 weight %;
c. Silicon dioxide in the range of about 0 to about 3 weight %; and
d. Solid UFP in the range of about 3 to about 15 weight %, wherein the UFP is a polymethyl urea resin, and the UFP is coated with the NBPT.
4. The composition of claim 3 wherein the composition further comprises an aqueous urea solution.
5. The composition of claim 3 , wherein the NBPT is at least about 50 weight % pure.
6. The composition of claim 5 , further comprising an amide solvent.
7. The composition of claim 3 , wherein the UFP is an unrefined polymethyl urea resin.
8. The composition of claim 3 , wherein the composition further comprises a dye product.
9. A method of preparing the composition of claim 2 comprising:
a. Coating the solid UFP with the NBPT, wherein the NBPT is molten or in a suspension or solution;
b. Adding the DCD; and
c. Optionally adding silicon dioxide; wherein the final ranges of the components are NBPT in the range of about 0.4 to about 15 weight %; DCD in the range of about 40 to about 95 weight %; silicon dioxide in the range of about 0 to 3 weight %; and UFP in the range of about 3 to about 15 weight %.
10. The method of claim 9 , wherein the composition is mixed with an aqueous urea to provide a fluid urea-based fertilizer having the following composition:
a. NBPT in the range of about 0.004 to about 1.5 weight %;
b. DCD in the range of about 0.04 to about 0.85 weight %;
c. silicon dioxide in the range of about 0 to about 0.03 weight %;
d. solid UFP in the range of about 0.03 to about 0.30 weight %; and
e. an aqueous urea in the range of about 98 to about 99.5 weight %.
11. The method of claim 10 , wherein the aqueous urea is urea ammonium nitrate (UAN).
12. A method of preparing the composition of claim 3 comprising:
a. Coating the solid UFP with the NBPT, wherein the NBPT is molten or in a suspension or solution;
b. Blending the DCD and UFP;
c. Blending the UFP and NBPT together with the UFP and DCD; and
d. Optionally adding silicon dioxide; wherein the final ranges of the components are NBPT in the range of about 0.4 to about 15 weight %; DCD in the range of about 40 to about 95 weight %; silicon dioxide in the range of about 0 to about 3 weight %; and UFP in the range of about 3 to about 15 weight %.