View Patent ↗A golf ball has a cover with a Shore D hardness of at least about 59 and a coating on the cover that has at least one of (a) a pencil hardness of 2 B or less, (b) a Sward hardness of about 40 or less, or (c) a Hit (Young's Modulus)<20 N/mm 2 and h max >0.55 micrometer.
1. A golf ball, comprising a cover with a Shore D hardness of about 60 to about 76 and a coating on the cover, wherein the coating has a pencil hardness of 7B to 4B.
2. A golf ball according to claim 1 , wherein the coating has a pencil hardness of 5B to 4B.
3. A golf ball according to claim 1 , wherein the coating is free of pigment and filler.
4. A golf ball according to claim 1 , wherein the coating comprises a polyurethane.
5. A golf ball according to claim 4 , wherein the polyurethane is a reaction product of (a) at least one polyisocyanate, (b) at least one polymeric polyol, (c) optionally, at least one extender with two or more isocyanate-reactive groups, and (d) optionally, a polysiloxane or fluoropolymer having at least one functional group reactive with at least one of components (a)-(c).
6. A golf ball according to claim 5 , wherein the component (a) comprises a biuret of an aliphatic diisocyanate.
7. A golf ball according to claim 1 , wherein the coating comprises a polyurethane that is the reaction product of an aliphatic biuret, a linear polyester diol, and a branched polyester polyol.
8. A golf ball according to claim 1 , wherein the cover comprises a thermoset polyurethane or a partially crosslinked thermoplastic polyurethane.
9. A method of making a golf ball, comprising coating a golf ball having a cover with a coating composition comprising (a) at least one polyisocyanate, (b) at least one polymeric polyol, (c) optionally, at least one extender with two or more isocyanate-reactive groups, and (d) a polysiloxane or fluoropolymer having at least one functional group reactive with at least one of components (a)-(c),
wherein the cover has a Shore D hardness of about 60 to about 76 and
wherein the coating composition is reacted to produce a coating having a pencil hardness of 7B to 4B.