Titanium alloy having good oxidation resistance and high strength at elevated temperatures
View Patent ↗A titanium alloy may be characterized by a good oxidation resistance, high strength and creep resistance at elevated temperatures up to 750° C., and good cold/hot forming ability, good superplastic forming performance, and good weldability. The alloy may contain, in weight percent, aluminum 4.5 to 7.5, tin 2.0 to 8.0, niobium 1.5 to 6.5, molybdenum 0.1 to 2.5, silicon 0.1 to 0.6, oxygen up to 0.20, carbon up to 0.10, and balance titanium with incidental impurities.
1. A high temperature titanium alloy comprising:
5.0 to 7.0% aluminum by weight;
3.0 to 6.0% tin by weight;
2.5 to 6.0% niobium by weight;
0.1 to 1.5% molybdenum by weight;
0.1 to 0.6% silicon by weight
zirconium below 0.1% by weight;
no more than 0.20% oxygen;
no more than 0.10% carbon;
iron, nickel, chromium, copper and manganese are each below 0.1% by weight and a total of <0.3 combined;
hafnium and rhenium in a range of 0.0 to 0.3% by weight and <0.3 combined and
a balance titanium.
2. The alloy of claim 1 wherein aluminum is 5.5 to 6.5% by weight; tin is 3.5 to 4.5% by weight; niobium is 3.0 to 3.25% by weight; molybdenum is 0.5 to 0.8% by weight; silicon is 0.30 to 0.45% by weight; oxygen is 0.08 to 0.12% by weight; carbon is 0.02 to 0.04% by weight.
3. The alloy of claim 1 wherein the alloy comprises a total of zirconium and vanadium in a range of 0.0 to 0.5% by weight.
4. The alloy of claim 1 wherein the alloy has an ultimate tensile strength of at least 260 at a temperature of about 750° C.
5. The alloy of claim 1 wherein the alloy has a yield strength of at least 150 at a temperature of about 750° C.
6. The alloy of claim 1 wherein the alloy has a weight gain of no more than 2.00 mg/cm 2 after maintaining the alloy in air continuously at a temperature of about 750° C. for a duration of 208 hours.
7. The alloy of claim 1 wherein the alloy has an alpha case depth of no more than about 100 microns after maintaining the alloy in air continuously at a temperature of about 750° C. for 208 hours.
8. The alloy of claim 1 wherein the alloy at a temperature of about 25° C. has a percent elongation of at least 2% after exposure in air to a temperature of 750° C. for 100 hours.
9. The alloy of claim 1 wherein the alloy comprises no more than 0.1 weight percent of vanadium.
10. The alloy of claim 1 , further comprising tantalum within the range of 0.0 to 1.0% by weight and wherein tin is 4.0-6.0% by weight.
11. The alloy of claim 1 wherein aluminum is 5.5 to 6.5% by weight; tin is 3.5 to 4.5% by weight; niobium is 4-6% by weight; molybdenum is 0.5 to 0.8% by weight; silicon is 0.30 to 0.45% by weight; oxygen is 0.08 to 0.12% by weight; and carbon is 0.03 to 0.04% by weight.
12. An aircraft engine component formed from the alloy of claim 1 .
13. The aircraft engine component of claim 12 wherein the aircraft engine component comprises at least a portion of one of an aircraft engine nacelle, an aircraft engine casing, an aircraft engine rotary compressor blade, an aircraft engine stator vane, an aircraft engine rotary turbine blade, an aircraft engine exhaust nozzle, an aircraft engine exhaust plug and an aircraft engine fastener.
14. A portion of a heat shield of an aircraft engine pylon formed from the alloy of claim 1 .
15. An internal combustion engine component formed from the alloy of claim 1 .
16. The internal combustion engine component of claim 15 wherein the internal combustion engine component is a valve.
17. A component of a gas turbine engine formed from the alloy of claim 1 .
18. A component having an operational temperature of at least about 600° C. formed from the alloy of claim 1 .
19. A high temperature titanium alloy comprising:
5.0 to 7.0% aluminum by weight;
3.0 to 6.0% tin by weight;
2.5 to 6.0% niobium by weight;
0.1 to 1.5% molybdenum by weight;
0.1 to 0.6% silicon by weight;
zirconium below 0.1% by weight;
a total of zirconium and vanadium in a range of 0.0 to 0.5% by weight;
a total of hafnium and rhenium in a range of 0.0 to 0.3% by weight; and a balance titanium.
20. The alloy of claim 19 wherein the alloy comprises no more than 0.1 weight percent of vanadium.
21. The alloy of claim 19 wherein the alloy comprises
no more than 0.20 weight percent of oxygen;
no more than 0.10 weight percent of carbon;
no more than 0.10 weight percent of each of nickel, iron, chromium, copper and manganese.
22. The alloy of claim 19 wherein
aluminum is 5.5 to 6.5% by weight;
tin is 3.5 to 4.5% by weight;
niobium is 2.75 to 3.25% by weight;
molybdenum is 0.5 to 0.8% by weight;
silicon is 0.30 to 0.45% by weight;
oxygen is 0.08 to 0.12% by weight;
carbon is 0.02 to 0.04% by weight;
each of nickel, iron, chromium, copper and manganese is no more than 0.10% by weight.
23. The alloy of claim 19 , further comprising tantalum within the range of 0.0 to 1.0% by weight.