Particulate superabsorbent polymer composition having improved stability
The present invention relates to a particulate superabsorbent polymer composition having improved stability comprising a polymer comprising from about 0.01 wt % to about 5 wt % of a neutralized aluminum salt solution applied to the surface of a particulate superabsorbent polymer; wherein an aqueous solution of the neutralized aluminum salt has a pH value from about 5.5 to about 8 and the particulate superabsorbent polymer composition has an original Free Swell Gel Bed Permeability (FSGBP) of about 20×10 −8 cm 2 to about 200×10 −8 cm 2 and a compressibility of from about 1.30 mm 2 /N to about 4 mm 2 /N prior to subjecting the particulate superabsorbent polymer composition to a Processing Test; and subsequent to subjecting the particulate superabsorbent polymer composition to the Processing Test, the particulate superabsorbent polymer composition has a permeability stability index of from about 0.60 to about 0.99.
1. A particulate superabsorbent polymer composition having improved stability comprising a particulate superabsorbent polymer and from 0.01 wt % to about 5 wt % based on the particulate superabsorbent polymer composition weight of a neutralized aluminum salt applied to the surface of the particulate superabsorbent polymer, in the form of an aqueous neutralized aluminum salt solution having a pH value from about 5.5 to about 8; wherein the particulate superabsorbent polymer composition has a Centrifuge Retention Capacity (CRC) of from about 25 grams to about 40 grams of 0.9 weight percent sodium chloride aqueous per gram of the particulate superabsorbent polymer composition, wherein the CRC is measured either before or after subjecting the superabsorbent polymer composition to a Processing Test, and an original Free Swell Gel Bed Permeability (FSGBP) of from about 20×10 −8 cm 2 to about 200×10 −8 cm 2 prior to subjecting the particulate superabsorbent polymer composition to the Processing Test; and a compressibility of from 1.30 mm 2 /N to about 4 mm 2 /N and a permeability stability index of from 0.60 to about 0.99 when subjecting the particulate superabsorbent polymer composition to a Processing Test.
2. The particulate superabsorbent polymer composition having improved stability according to claim 1 wherein said particulate superabsorbent polymer composition has a permeability stability index of from 0.70 to about 0.99.
3. The particulate superabsorbent polymer composition having improved stability according to claim 1 wherein said aqueous neutralized aluminum salt solution has a pH value from about 6 to about 7.
4. The particulate superabsorbent polymer composition having improved stability according to claim 1 wherein said neutralized aluminum salt is selected from:
a) the reaction product of sodium hydroxide with aluminum sulfate or aluminum sulfate hydrate;
b) the reaction product of an organic acid and sodium aluminate;
c) the reaction product of sodium aluminate and aluminum sulfate or aluminum sulfate hydrate; or
d) the reaction product of an organic acid or its salt and sodium aluminate and aluminum sulfate or aluminum sulfate hydrate.
5. A particulate superabsorbent polymer composition having improved stability comprising:
a) from about 55 wt % to about 85 wt % of polymerizable unsaturated acid group containing monomers selected from acrylic acid, methacrylic acid, or 2-acrylamido-2-methylpropanesulfonic acid, or mixtures thereof;
b) from about 14 wt % to about 45 wt % of an alkali base selected from sodium hydroxide or potassium hydroxide to neutralize the polymerizable unsaturated acid group containing monomers of a) to from about 50 to about 80 mol %;
c) from about 0.001 wt % to about 5.0 wt % based on the weight of a) of an internal crosslinking agent, wherein the components a), b) and c) are polymerized into a hydrogel which is granulated into particulate superabsorbent polymer having a surface;
d) from about 0.001 wt % to about 5.0 wt % based on the particulate superabsorbent composition weight of surface crosslinking agent applied to the surface of the particulate superabsorbent polymer;
e) from 0.001 wt to about 5.0 wt % based on the particulate superabsorbent composition weight of a neutralized aluminum salt applied to the surface of the particulate superabsorbent polymer, in the form of an aqueous neutralized aluminum salt solution having a pH value from about 5.5 to about 8;
wherein the particulate superabsorbent polymer composition has a Centrifuge Retention Capacity of from about 25 grams to about 40 grams of 0.9 weight percent sodium chloride aqueous per gram of the particulate superabsorbent polymer composition, wherein the CRC is measured either before or after subjecting the particulate superabsorbent polymer composition to a Processing Test, and an original Free Swell Gel Bed Permeability (FSGBP) of about 20×10 −8 cm 2 to about 200×10 −8 cm 2 prior to subjecting the particulate superabsorbent polymer composition to the Processing Test; and has a permeability stability index of from 0.60 to about 0.99 when subjecting the particulate superabsorbent polymer composition to a Processing Test and a compressibility of from about 1.30 mm 2 /N to about 4 mm 2 /N.
6. The particulate superabsorbent polymer composition having improved stability according to claim 5 wherein said aqueous neutralized aluminum salt solution has a pH value from about 6 to about 7.
7. The particulate superabsorbent polymer composition having improved stability according to claim 5 wherein said neutralized aluminum salt is selected from:
a) the reaction product of sodium hydroxide with aluminum sulfate or aluminum sulfate hydrate;
b) the reaction product of an organic acid with sodium aluminate;
c) the reaction product of sodium aluminate with aluminum sulfate or aluminum sulfate hydrate; or
d) the reaction product of an organic acid or its salt with sodium aluminate and aluminum sulfate or aluminum sulfate hydrate.
8. The particulate superabsorbent polymer composition having improved stability according to claim 5 having a permeability stability index of from 0.70 to about 0.99.
9. The particulate superabsorbent polymer composition having improved stability according to claim 7 said organic acid is selected from glycolic acid, lactic acid or gluconic acid.
10. A process for the production of a particulate superabsorbent polymer composition having improved stability according to claim 1 comprising the following steps:
a) providing a particulate superabsorbent polymer;
b) preparing a neutralized aluminum salt in the form of an aqueous solution having a pH value from about 5.5 to about 8; and;
c) applying the aqueous neutralized aluminum salt solution on the surface of the particulate superabsorbent polymer; and
wherein the particulate superabsorbent polymer composition has a degree of neutralization of from about 50% mol to about 80 mol %; and the particulate superabsorbent polymer composition has a Centrifuge Retention Capacity of from about 25 grams to about 40 grams of 0.9 weight percent sodium chloride aqueous per gram of the particulate superabsorbent polymer composition, wherein the CRC is measured either before or after subjecting the superabsorbent polymer composition to a Processing Test, and a Free Swell Gel Bed Permeability (FSGBP) of about 20×10 −8 cm 2 to about 200×10 −8 cm 2 prior to subjecting the treated particulate superabsorbent polymer composition to the Processing Test; and a compressibility from 1.30 mm 2 /N to about 4 mm 2 /N and a permeability stability index of from 0.60 to about 0.99 when subjecting the particulate superabsorbent polymer composition to a Processing Test.
11. The process according to claim 10 wherein said particulate superabsorbent polymer composition has a permeability stability index of from 0.70 to about 0.99 when subjecting the particulate superabsorbent polymer composition to a Processing Test.
12. The process according to claim 10 wherein said aqueous aluminum salt solution has a pH value from about 6 to about 7.
13. The process according to claim 10 wherein said neutralized aluminum salt is selected from:
a) the reaction product of sodium hydroxide with aluminum sulfate or aluminum sulfate hydrate;
b) the reaction product of an organic acid with sodium aluminate;
c) the reaction product of sodium aluminate with aluminum sulfate or aluminum sulfate hydrate; or
d) the reaction product of an organic acid or its salt with sodium aluminate and aluminum sulfate or aluminum sulfate hydrate.