Photo-curable resin compositions and method of using the same in three-dimensional printing for manufacturing artificial teeth and denture base
Photo-curable compositions for artificial teeth and denture base and a method for manufacturing denture by a three-dimensional printing system are provided. The compositions include photo-curable organic compounds, surface modified nano-sized inorganic filler, photo-initiator, colorant, and stabilizer. The composition is in a viscous liquid state having 1500-5000 cps at ambient temperature and has a low viscosity of 50-500 cps at jetting temperature or dispensing temperature. The composition also has an excellent curing rate for three-dimensional printing. Using the compositions, denture having a distinctive denture base and a set of artificial teeth can be manufactured via an inkjet type or digital light process type three-dimensional printing according to Computer Aided Design (CAD) data.
1. A composition comprising:
about 50 to about 75 weight % of at least one kind of ethoxylated difunctional bisphenol A dimethacrylate;
about 5 to about 15 weight % of at least one kind of multifunctional methacrylate having two or more methacryloxy groups;
about 15 to about 35 weight % of at least one kind of urethane dimethacrylate;
about 5 to about 35 weight % of at least one kind of silica-based fine particles having methacrylate functionalization layers and having an average particle size of less than about 200 nm;
about 0.2 to about 5.0 weight % of at least one kind of ultraviolet/visible (UV/Vis) light-photo-polymerization initiator;
at least one colorant; and
at least one stabilizer,
wherein viscosity of a liquid state mixture, including the at least one kind of ethoxylated difunctional bisphenol A dimethacrylate, the at least one kind of multifunctional methacrylate, the at least one kind of urethane dimethacrylate, the at least one kind of silica-based fine particles, the at least one kind of UV/Vis light-photo-polymerization initiator, the at least one colorant, and the at least one stabilizer, is from 2000-5200 centipoise (cps) at room temperature and from 50 to 500 cps at 70° C., and
wherein the viscosity is adjusted by controlling a ratio of the at least one kind of ethoxylated difunctional bisphenol A dimethacrylate, the at least one kind of multifunctional methacrylate, the at least one kind of urethane dimethacrylate, the at least one kind of silica-based fine particles, the at least one kind of UV/Vis light-photo-polymerization initiator, the at least one colorant, and the at least one stabilizer in the mixture.
2. A composition comprising:
about 40 to about 60 weight % of at least one kind of ethoxylated difunctional bisphenol A dimethacrylate;
about 5 to about 20 weight % of at least one kind of multifunctional methacrylate;
about 20 to about 45 weight % of at least one kind of urethane dimethacrylate;
about 0 to about 15 weight % of at least one kind of silica-based fine particles having methacrylate functionalization layers and having an average particle size of less than about 200 nm;
about 0.2 to about 5.0 weight % of at least one kind of ultraviolet/visible (UV/Vis) light-photo-polymerization initiator;
at least one colorant; and
at least one stabilizer,
wherein viscosity of a liquid state mixture, including the at least one kind of ethoxylated difunctional bisphenol A dimethacrylate, the at least one kind of multifunctional methacrylate, the at least one kind of urethane dimethacrylate, the at least one kind of silica-based fine particles, the at least one kind of UV/Vis light-photo-polymerization initiator, the at least one colorant, and the at least one stabilizer, is from 2000-5200 centipoise (cps) at room temperature and from 50 to 500 cps at 70° C., and
wherein the viscosity is adjusted by controlling a ratio of the at least one kind of ethoxylated difunctional bisphenol A dimethacrylate, the at least one kind of multifunctional methacrylate, the at least one kind of urethane dimethacrylate, the at least one kind of silica-based fine particles, the at least one kind of UV/Vis light-photo-polymerization initiator, the at least one colorant, and the at least one stabilizer in the mixture.
3. The composition of claim 1 , wherein the light-photo-polymerization initiator comprises acylphosphine oxide compounds.
4. The composition of claim 1 , wherein the silica-based fine particles comprise reactive silica particles that are surface-modified by a surface modifying agent.
5. The composition of claim 4 , wherein the surface modifying agent comprises compounds containing methacryloxy groups.
6. A method of printing a denture using the composition of claim 1 , the method comprising:
stacking layers of the mixture and curing the stacked layers one-by-one using a three-dimensional printer based on Computer-Aided Design/Computer-Aided Manufacturing (CAD/CAM) generated information that is related to the denture to be manufactured.
7. The method of claim 6 , wherein the three-dimensional printer is operated according to an ink-jet printing method or a digital light processing method.
8. The method of claim 6 , wherein the information comprises a digital model generated based on a dental impression of a patent's mouth and a CAD/CAM design.
9. The method of claim 6 , further comprising performing post-treatment to the printed denture to improve surface quality of the denture.
10. The method of claim 6 , further comprising performing a post-curing operation on the printed denture at about 30 to about 160° C.
11. The method of claim 6 , wherein the denture comprises a printed denture base portion and a printed artificial tooth portion formed as a single body.
12. The method of claim 6 , further comprising assembling a denture base and artificial teeth with dental adhesives after using the three-dimensional printer to separately print the denture base and the artificial teeth.
13. The method of claim 6 , wherein the denture comprises a partial denture and a full denture.
14. A method for manufacturing a denture using a three-dimensional printer and light-curable materials based on denture information, the method comprising:
manufacturing a denture base from a first composition; and
manufacturing at least one artificial tooth from a second composition that is different from the first composition,
wherein:
the first composition comprises:
about 40 to about 60 weight % of at least one kind of ethoxylated difunctional bisphenol A dimethacrylate;
about 5 to about 20 weight % of at least one kind of multifunctional methacrylate;
about 20 to about 45 weight % of at least one kind of urethane dimethacrylate;
about 0 to about 15 weight % of at least one kind of a silica-based fine particles having methacrylate functionalization layers and having an average particle size of less than about 200 nm;
about 0.2 to about 5.0 weight % of at least one kind of ultraviolet/visible (UV/Vis) light-photo-polymerization initiator;
at least one colorant; and
at least one stabilizer,
wherein viscosity of a first liquid state mixture, including the at least one kind of ethoxylated difunctional bisphenol A dimethacrylate, the at least one kind of multifunctional methacrylate, the at least one kind of urethane dimethacrylate, the at least one kind of silica-based fine particles, the at least one kind of UV/Vis light-photo-polymerization initiator, the at least one colorant, and the at least one stabilizer, is from 2000-5200 centipoise (cps) at room temperature and from 50 to 500 cps at 70° C., and
wherein the viscosity of the first liquid state mixture is adjusted by controlling a ratio of the at least one kind of ethoxylated difunctional bisphenol A dimethacrylate, the at least one kind of multifunctional methacrylate, the at least one kind of urethane dimethacrylate, the at least one kind of silica-based fine particles, the at least one kind of UV/Vis light-photo-polymerization initiator, the at least one colorant, and the at least one stabilizer in the mixture; and
the second composition comprises:
about 50 to about 75 weight % of at least one kind of ethoxylated difunctional bisphenol A dimethacrylate;
about 5 to about 15 weight % of at least one kind of multifunctional methacrylate having two or more methacryloxy groups;
about 15 to about 35 weight % of at least one kind of urethane dimethacrylate;
about 5 to about 35 weight % of at least one kind of a silica-based fine particles having or methacrylate functionalization layers and having an average particle size of less than about 200 nm;
about 0.2 to about 5.0 weight % of at least one kind of ultraviolet/visible (UV/Vis) light-photo-polymerization initiator;
at least one colorant; and
at least one stabilizer,
wherein viscosity of a second liquid state mixture, including the at least one kind of ethoxylated difunctional bisphenol A dimethacrylate, the at least one kind of multifunctional methacrylate, the at least one kind of urethane dimethacrylate, the at least one kind of silica-based fine particles, the at least one kind of UV/Vis light-photo-polymerization initiator, the at least one colorant, and the at least one stabilizer, is from 2000-5200 centipoise (cps) at room temperature and from 50 to 500 cps at 70° C., and
wherein the viscosity of the second liquid state mixture is adjusted by controlling a ratio of the at least one kind of ethoxylated difunctional bisphenol A dimethacrylate, the at least one kind of multifunctional methacrylate, the at least one kind of urethane dimethacrylate, the at least one kind of silica-based fine particles, the at least one kind of UV/Vis light-photo-polymerization initiator, the at least one colorant, and the at least one stabilizer in the mixture.