Copolymer blend compositions for use to increase paper filler content
View Patent ↗Disclosed are methods for increasing the filler content of paper or paperboard, comprising (a) combining a heterogeneous polymer blend with a ground calcium carbonate filler; (b) combining the resulting mixture with a pulp slurry; and (c) processing the resulting slurry mixture to form a sheet of paper or paperboard. Also disclosed are methods of increasing the filler content of paper or paperboard comprising (1) combining either a heterogeneous polymer blend or a ground calcium carbonate filler with a pulp slurry, (2) combining the remaining component with the pulp slurry; and (c) processing the resulting pulp slurry mixture to form a sheet of paper or paperboard.
1. A method of increasing the filler content of a sheet of paper or paperboard, comprising
A) combining either (i) a heterogeneous polymer blend or (ii) a ground calcium carbonate filler with a pulp slurry to form a mixture;
B) combining the remaining component (i) or (ii) from step (a) with a pulp slurry mixture and
C) processing the resulting pulp slurry mixture to form a sheet of paper or paperboard, and
wherein the heterogeneous polymer blend comprises:
a) one or more anionic polymers formed from monomer(s) selected from the group consisting of: (1) acrylic acid, (2) methacrylic acid, (3) styrenesulfonic acid, (4) vinylsulfonic acid, (5) acrylamidomethylpropane sulfonic acid, and (6) mixtures thereof;
b) one or more cationic polymers formed from monomer(s) selected from the group consisting of: (1) diallyldimethylammonium chloride, (2) acryloylethyltrimethyl ammonium chloride, (3) methacryloylethyl trimethyl ammonium chloride, (4) acryloylethyltrimethylammonium sulfate, (5) methacryloylethyl trimethyl ammonium sulfate, (6) acrylamidopropyltrimethyl ammonium chloride, (7) methacrylamidopropyl trimethyl ammonium chloride, (8) non-quaternized forms of (2)-(7), (9) vinylformamide (subsequently hydrolyzed to vinylamine), and (10) mixtures thereof; and
c) one or more nonionic polymers formed from monomer(s) selected from the group consisting of: (1) acrylamide, (2) methacrylamide, (3) N-alkylacrylamide, (4) vinylformamide, and (5) mixtures thereof.
2. The method of claim 1 wherein the heterogeneous polymer blend further comprises (d) one or more copolymers comprising at least one anionic monomer and at least one non-ionic monomer; and (e) one or more copolymers comprising at least one cationic monomer and at least one non-ionic monomer.
3. The method of claim 2 wherein the heterogeneous polymer blend reaction product further comprises (f) one or more terpolymers comprising at least one anionic monomer, at least one cationic monomer, and at least one non-ionic monomer.
4. The method of claim 1 wherein the anionic monomer is acrylic acid.
5. The method of claim 1 wherein the cationic monomer is diallyldimethylammonium chloride.
6. The method of claim 1 wherein the nonionic monomer is acrylamide.
7. The method of claim 1 wherein the molar reactant ratio of anionic monomer, nonionic monomer and cationic monomer is in the range of from about 10 to 30 mol % anionic monomer, from about 40 to about 80 mol % nonionic monomer and from about 10 to about 30 mol % cationic monomer.
8. The method of claim 1 wherein the amount of heterogeneous polymer blend is from 0.05 to about 1 wt % relative to the total dry weight of the pulp slurry.
9. The method of claim 1 wherein the molar reactant ratio of anionic monomer, nonionic monomer and cationic monomer is in the range of from about 10 to 30 mol % anionic monomer, from about 40 to about 80 mol % nonionic monomer and from about 10 to about 30 mol % cationic monomer.
10. A method of increasing the filler content of a sheet of paper or paperboard, comprising
A) combining a heterogeneous polymer blend with a ground calcium carbonate filler to form a mixture;
B) combining the mixture of A) with a pulp slurry mixture, and
C) processing the resulting pulp slurry mixture to form a sheet of paper or paperboard, and
wherein the heterogeneous polymer blend comprises:
a) one or more anionic polymers formed from monomer(s) selected from the group consisting of: (1) acrylic acid, (2) methacrylic acid, (3) styrenesulfonic acid, (4) vinylsulfonic acid, (5) acrylamidomethylpropane sulfonic acid, and (6) mixtures thereof;
b) one or more cationic polymers formed from monomers) selected from the group consisting of: (1) diallyldimethylammonium chloride, (2) acryloylethyltrimethyl ammonium chloride, (3) methacryloylethyl trimethyl ammonium chloride, (4) acryloylethyltrimethylammonium sulfate, (5) methacryloylethyl trimethyl ammonium sulfate, (6) acrylamidopropyltrimethyl ammonium chloride, (7) methacrylamidopropyl trimethyl ammonium chloride, (8) non-quaternized forms of (2)-(7), (9) vinylformamide (subsequently hydrolyzed to vinylamine), and (10) mixtures thereof; and
c) one or more nonionic polymers formed from monomer(s) selected from the group consisting of: (1) acrylamide, (2) methacrylamide, (3) N-alkylacrylamide, (4) vinylformamide, and (5) mixtures thereof.
11. The method of claim 10 wherein the heterogeneous polymer blend further comprises (d) one or more copolymers comprising at least one anionic monomer and at least one non-ionic monomer; and (e) one or more copolymers comprising at least one cationic monomer and at least one non-ionic monomer.
12. The method of claim 11 wherein the heterogeneous polymer blend reaction product further comprises (f) one or more terpolymers comprising at least one anionic monomer, at least one cationic monomer, and at least one non-ionic monomer.
13. The method of claim 10 wherein the anionic monomer is acrylic acid.
14. The method of claim 10 wherein the cationic monomer is diallyldimethylammonium chloride.
15. The method of claim 10 wherein the nonionic monomer is acrylamide.
16. The method of claim 10 wherein the amount of heterogeneous polymer blend is from 0.05 to about 1 wt % relative to the total dry weight of the pulp slurry.
17. A method of increasing the filler content of a sheet of paper or paperboard by:
a) combining a mixture of poly-diallyldimethylammonium chloride polymer and an acrylamide/acrylate copolymer with a ground calcium carbonate filler;
b) combining the resulting mixture from step (a) with a pulp slurry; and
c) processing the resulting pulp slurry mixture to form a sheet of paper or paperboard.