Fluorination of Fluoropolymer Resin to Reduce Discoloration
Process for reducing thermally induced discoloration of fluoropolymer resin produced by polymerizing fluoromonomer in an aqueous medium to form aqueous fluoropolymer dispersion and isolating said fluoropolymer from said aqueous medium to obtain said fluoropolymer resin. The process comprises: exposing the fluoropolymer resin to fluorine.
1 . Process for reducing thermally induced discoloration of fluoropolymer resin, said fluoropolymer resin produced by polymerizing fluoromonomer in an aqueous dispersion medium to form aqueous fluoropolymer dispersion and isolating said fluoropolymer from said aqueous medium to obtain said fluoropolymer resin, said process comprising:
exposing the fluoropolymer resin to fluorine.
2 . The process of claim 1 wherein said process reduces thermally induced discoloration by at least about 10% as measured by % change in L* on the CIELAB color scale.
3 . The process of claim 1 wherein said aqueous fluoropolymer dispersion contains hydrocarbon surfactant which causes said thermally induced discoloration.
4 . The process of claim 3 wherein said aqueous fluoropolymer dispersion is polymerized in the presence of hydrocarbon surfactant.
5 . The process of claim 1 wherein said fluoropolymer resin is melt-processible.
6 . The process of claim 5 wherein said exposing of said fluoropolymer resin to fluorine is carried out above the melting point of the fluoropolymer resin.
7 . The process of claim 6 wherein said exposing the fluoropolymer resin to fluorine is carried out with the fluoropolymer resin heated to a temperature above its melting point up to about 400° C.
8 . The process of claim 1 wherein said exposing of said fluoropolymer resin to fluorine is carried out below the melting point of the fluoropolymer resin.
9 . The process of claim 8 wherein said exposing fluoropolymer resin to fluorine is carried out with the fluoropolymer resin heated to a temperature of about 20° C. to about 250° C.
10 . The process of claim 1 wherein the fluoropolymer resin has an initial thermally induced discoloration value (L* i ) at least about 4 L units on the CIELAB color scale below the L* value of equivalent fluoropolymer resin of commercial quality manufactured using ammonium perfluorooctanoate fluorosurfactant.