Cathode active material, method of manufacturing the same and battery
View Patent ↗A cathode active material capable of obtaining a high capacity and capable of improving stability or low-temperature characteristics, a method of manufacturing the same, and a battery are provided. A cathode ( 21 ) includes a cathode active material including a lithium complex oxide including Li and at least one kind selected from the group consisting of Co, Ni and Mn, and P and at least one kind selected from the group consisting of Ni, Co, Mn, Fe, Al, Mg and Zn as coating elements on a surface of the lithium complex oxide. Preferably, the contents of the coating elements are higher on the surface of the cathode active material than those in the interior thereof, and decrease from the surface to the interior.
1. A cathode active material comprising:
a lithium complex oxide represented by Chemical Formula 3:
Li z Mn 2-g M3 g O 4-h
wherein M3 represents at least one kind selected from the group consisting of cobalt, nickel, magnesium, aluminum, boron, titanium, vanadium, chromium, iron, copper, zinc, molybdenum, tin, calcium, strontium and tungsten, the values of z, g and h are within ranges of 0.8≦z≦1.2, 0≦g<1.0 and −0.2≦h≦0.2, respectively; and
a surface layer comprising aluminum phosphate formed on a surface of the lithium complex oxide,
wherein the surface layer is within a range from 0.2 mol % to 6.0 mol % both inclusive in total relative to the lithium complex oxide, and
wherein an atomic ratio of phosphorus to aluminum in the surface layer is within a range from 0.35 to 12.7 both inclusive.
2. The cathode active material according to claim 1 , comprising a central section comprising the lithium complex oxide, the surface layer being arranged on at least a part of the central section.
3. The cathode active material according to claim 1 , wherein the lithium complex oxide further comprises at least one selected from Chemical Formula 1:
Li x Co a M1 b O 2-c
wherein M1 represents at least one kind selected from the group consisting of nickel (Ni), manganese (Mn), magnesium (Mg), aluminum (Al), boron (B), titanium (Ti), vanadium (V), chromium (Cr), iron, copper (Cu), zinc (Zn), molybdenum (Mo), tin (Sn), calcium (Ca), strontium (Sr), tungsten (W), zirconium (Zr) and silicon (Si), the values of x, a, b and c are within ranges of 0.8≦x≦1.2, 0.8≦a≦1, 0≦b≦0.2 and −0.1≦c≦0.2, respectively; and Chemical Formula 2:
Li y Ni d M2 e O 2-f
wherein M2 represents at least one kind selected from the group consisting of cobalt, manganese, magnesium, aluminum, boron, titanium, vanadium, chromium, iron, copper, zinc, molybdenum, tin, calcium, strontium, tungsten, zirconium and silicon, the values of y, d, e and f are within ranges of 0.8≦y≦1.2, 0.3≦d≦0.98, 0.02≦e≦0.7 and −0.1≦f≦0.2, respectively.
4. A battery comprising:
a cathode;
an anode; and
an electrolyte,
wherein the cathode comprises a cathode active material represented by Chemical Formula 3:
Li z Mn 2-g M3 g O 4-h
wherein M3 represents at least one kind selected from the group consisting of cobalt, nickel, magnesium, aluminum, boron, titanium, vanadium, chromium, iron, copper, zinc, molybdenum, tin, calcium, strontium and tungsten, the values of z, g and h are within ranges of 0.8≦z≦1.2, 0≦g<1.0 and −0.2≦h≦0.2, respectively; and
a surface layer comprising aluminum phosphate formed on a surface of the cathode active material,
wherein the surface layer is within a range from 0.2 mol % to 6.0 mol % both inclusive in total relative to the lithium complex oxide, and
wherein an atomic ratio of phosphorus to aluminum in the surface layer is within a range from 0.35 to 12.7 both inclusive.
5. The battery according to claim 4 , wherein the cathode active material comprises a central section comprising the lithium complex oxide, the surface layer being arranged on at least a part of the central section.
6. The battery according to claim 4 , wherein the lithium complex oxide further comprises at least one selected from the group consisting of Chemical Formula 1:
Li x Co a M1 b O 2-c
(where M1 represents at least one kind selected from the group consisting of nickel (Ni), manganese (Mn), magnesium (Mg), aluminum (Al), boron (B), titanium (Ti), vanadium (V), chromium (Cr), iron (Fe), copper (Cu), zinc (Zn), molybdenum (Mo), tin (Sn), calcium (Ca), strontium (Sr), tungsten (W), zirconium (Zr) and silicon (Si), the values of x, a, b and c are within ranges of 0.8≦x≦1.2, 0.8≦a≦1, 0≦b≦0.2 and −0.1≦c≦0.2, respectively; and Chemical Formula 2:
Li y Ni d M2 e O 2-f
wherein M2 represents at least one kind selected from the group consisting of cobalt, manganese, magnesium, aluminum, boron, titanium, vanadium, chromium, iron, copper, zinc, molybdenum, tin, calcium, strontium, tungsten, zirconium and silicon, the values of y, d, e and f are within ranges of 0.8≦y≦1.2, 0.3≦d≦0.98, 0.02≦e≦0.7 and −0.1≦f≦0.2, respectively.
7. The battery according to claim 4 , wherein
the open circuit voltage in a fully charged state per a pair of the cathode and the anode is within a range from 4.25 V to 4.6 V both inclusive.
8. A method of manufacturing a cathode active material, the method comprising:
providing a lithium complex oxide particle represented by Chemical Formula 3:
Li z Mn 2-g M3 g O 4-h
wherein M3 represents at least one kind selected from the group consisting of cobalt, nickel, magnesium, aluminum, boron, titanium, vanadium, chromium, iron, copper, zinc, molybdenum, tin, calcium, strontium and tungsten, the values of z, g and h are within ranges of 0.8≦z≦1.2, 0≦g<1.0 and −0.2≦h≦0.2, respectively; and
coating a particle surface of the lithium complex oxide with a surface layer comprising aluminum phosphate,
wherein the surface layer is within a range from 0.2 mol % to 6.0 mol % both inclusive in total relative to the lithium complex oxide, and
wherein an atomic ratio of phosphorus to aluminum in the surface layer is within a range from 0.35 to 12.7 both inclusive.