CERAMIC CUTTING TEMPLATE
The invention relates to a cutting template, to a cutting block, preferably a cutting template, and to a cutting block for use in medical technology.
1 .- 9 . (canceled)
10 . A ceramic cutting template, wherein said template comprises a base body having a recess therein for passing through and precisely guiding a cutting instrument, wherein the ceramic material comprises from 3 to 8% by weight of Y 2 O 3 , from 0 to 0.5% by weight of Al 2 O 3 , preferably 0.05 to 0.4% by weight of Al 2 O 3 , particularly preferred 0.1 to 0.3% by weight of Al 2 O 3 , and the balance to 100% by weight of ZrO 2 , and wherein up to 3% by weight of HfO 2 can be contained in ZrO 2 , and the monoclinic content in ZrO 2 is less than 2% by volume.
11 . The ceramic cutting template according to claim 10 , wherein the ceramic material has a strength of from 900 to 1600 MPa.
12 . The ceramic cutting template according to claim 10 , wherein the ceramic material has a grain size of <0.5 μm.
13 . The ceramic cutting template according to claim 10 , wherein the recess is slot-like.
14 . The ceramic cutting template according to claim 10 , wherein the recess is a through-hole.
15 . The ceramic cutting template according to claim 13 , wherein the slot-like recess comprises guiding surfaces that oppose each other.
16 . The ceramic cutting template according to claim 10 , wherein a through-hole is incorporated in the base body.
17 . A method of performing surgery on a bone comprising utilizing the ceramic cutting template according to claim 10 .
18 . The method of claim 17 , wherein said surgery is a knee TEP implantation.