View Patent ↗Multifunctional melamine epoxy resins, methylols and amines are provided. Methods of making multifunctional melamine epoxy resins, methylols and amines are also provided.
1. A carbon fiber composite comprising a cured epoxy resin of an epoxy resin and amino hardeners, wherein the epoxy resin is a compound of Formula III
wherein R 1 and R 2 are independently selected from the group consisting of:
R 3 is
2. The carbon fiber composite of claim 1 , wherein the epoxy resin has a Formula of
wherein R 3 is
3. The carbon fiber composite of claim 2 , wherein the epoxy resin has a Formula of
4. The carbon fiber composite of claim 2 , wherein the epoxy resin has a Formula of
5. The carbon fiber composite of claim 2 , wherein the epoxy resin has a Formula of
6. The carbon fiber composite of claim 2 , wherein the epoxy resin has a Formula of
7. The carbon fiber composite of claim 2 , wherein the epoxy resin has a Formula of
wherein R 3 is
8. An isocyanate terminated, cross-linked polyurethane, polyester, or silicone, wherein the isocyanate terminated polyurethane, polyester, or silicone are cross-linked with a compound of Formula III
wherein R 1 and R 2 are independently selected from the group consisting of CH 2 OH CH 2 NH 2 , and melaminyl, or are cross-linked with a compound having a formula of
9. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 8 , wherein the isocyanate terminated polyurethane, polyester, or silicone are cross-linked with a compound of Formula III
wherein R 1 and R 2 are independently selected from the group consisting of CH 2 OH, CH 2 NH 2 , and melaminyl.
10. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 9 , wherein R 1 and R 2 are CH 2 OH.
11. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 9 , wherein R 1 and R 2 are CH 2 NH 2 .
12. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 9 , wherein R 1 and R 2 are melaminyl.
13. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 8 , wherein the isocyanate terminated polyurethane, polyester, or silicone are cross-linked with a compound having a formula of:
14. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 13 , wherein the isocyanate terminated polyurethane, polyester, or silicone are cross-linked with a compound having a formula of
15. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 13 , wherein the isocyanate terminated polyurethane, polyester, or silicone are cross-linked with a compound having a formula of
16. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 13 , wherein the isocyanate terminated polyurethane, polyester, or silicone are cross-linked with a compound having a formula of
17. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 13 , wherein the isocyanate terminated polyurethane, polyester, or silicone are cross-linked with a compound having a formula of
18. The isocyanate terminated, cross-linked polyurethane, polyester, or silicone of claim 13 , wherein the isocyanate terminated polyurethane, polyester, or silicone are cross-linked with a compound having a formula of
19. A method of making a compound of Formula IV, the method comprising contacting hexamethylol melamine with ammonia to produce a compound of Formula IV,