Isomerisation catalyst preparation process
View Patent ↗A process for preparing an alkylaromatics isomerisation catalyst comprising at least 0.01% wt of platinum on a carrier comprising of from 1 to 9 wt % of ZSM-12 and inorganic binder, which process comprises treating the carrier with an impregnation solution comprising base and an anionic platinum complex which impregnation solution has a pH of from 5.5 to 8; and a process for the isomerisation of alkylaromatics with the help of catalyst thus obtained.
1. A process for preparing an alkylaromatics isomerization catalyst, comprising:
mixing an amount of ZSM-12 zeolite with an amount of an alumina binder to form a mixture, wherein said ZSM-12 zeolite has an average crystal size in the range of from 30 to 70 nm, a surface area of more than 250 m 2 /g as measured by nitrogen adsorption, and crystallinity of greater than 94%, and wherein the alumina of said alumina binder has a nitrogen pore volume of at least 0.6 cc/g and an average pore diameter greater than 80 Å;
shaping said mixture into extrudates;
without prior calcination of said extrudates, impregnating said extrudates with an impregnation solution comprising a base and an anionic platinum complex to provide impregnated extrudates, wherein said impregnation solution has a pH of from 5.5 to 8;
drying said impregnated extrudates; and
calcining the dried impregnated extrudates at a calcination temperature in the range of from 300 to 600° C. to provide said alkylaromatics isomerization catalyst;
wherein said amount of ZSM-12 zeolite and said amount of said alumina binder are such as to provide said alkylaromatics isomerization catalyst that comprises from 1 to 9 wt % ZSM-12 zeolite and more than 50 wt % alumina binder, based on the total weight of said alkylaromatics isomerization catalyst;
wherein the alkylaromatics isomerization catalyst provides an ethylbenzene conversion of at least 37% wt at a PXate of 95 wt %.
2. A process as claimed in claim 1 in which the base is a compound according to the formula (R 1 R 2 R 3 NH)OH in which the compounds R 1 , R 2 , R 3 each independently are chosen from the group consisting of hydrogen and alkyl containing of from 1 to 6 carbon atoms.
3. A process as claimed in claim 1 in which the impregnation is carried out by contacting the extrudates with an excess of impregnation solution while stirring.
4. A process as claimed in claim 1 in which a silica to alumina molar ratio of the ZSM-12 is in the range of from 60 to 200.
5. A process as claimed in claim 1 in which the anionic platinum complex is a platinum chloride complex of the general formula X n PtCl m , wherein X is either ammonium or hydrogen, n is an integer of from 1 to 6, and m is an integer of from 4 to 8.
6. A process as claimed in claim 1 , wherein the alumina binder is present in the alkylation isomerization catalyst in an amount of at least 90 wt %.
7. A process as claimed in claim 6 , wherein the alumina binder further comprises an additional compound selected from the group consisting of silica, titania, zirconia, ceria and gallia.
8. A process as claimed in claim 7 , wherein the alumina binder contains up to 50% wt of the additional compound.
9. A process as claimed in claim 8 , wherein a silica-to-alumina molar ratio of the ZSM-12 zeolite is in the range of from 70 to 150.
10. A process as claimed in claim 5 , wherein the platinum chloride complex is hexachloroplatinic acid.
11. A process as claimed in claim 10 , wherein the alumina binder is present in the extrudates in an amount of more than 80 wt %.
12. A process as claimed in claim 11 , wherein the alkylaromatics isomerization catalyst comprises from 1 to 7 wt % of the ZSM-12 zeolite.
13. A process as claimed in claim 12 , wherein the alumina binder further comprises an additional compound selected from the group consisting of silica, titania, zirconia, ceria and gallia.
14. A process as claimed in claim 13 , wherein the alumina binder contains up to 10% wt of the additional compound.
15. A process for preparing an alkylaromatics isomerization catalyst comprising:
mixing an amount of ZSM-12 zeolite with an amount of an alumina binder to form a mixture, wherein said ZSM-12 zeolite has an average crystal size in the range of from 30 to 70 nm, a surface area of more than 250 m 2 /g as measured by nitrogen adsorption, and crystallinity of greater than 94%, and wherein the alumina of said alumina binder has a nitrogen pore volume of at least 0.6 cc/g and an average pore diameter greater than 80 Å;
shaping said mixture into preformed carrier particles;
drying said preformed carrier particles;
calcining the dried preformed carrier particles at a calcination temperature in the range of from 300 to 600° C. to provide dried and calcined preformed carrier particles;
impregnating said dried and calcined preformed carrier particles with an impregnation solution comprising a base and an anionic platinum complex to provide impregnated preformed carrier particles, wherein said impregnation solution has a pH of from 5.5 to 8;
drying said impregnated preformed carrier particles; and
calcining the dried impregnated preformed carrier particles at a calcination temperature in the range of from 300 to 600° C. to provide said alkylaromatics isomerization catalyst;
wherein said amount of ZSM-12 zeolite and said amount of said alumina binder are such as to provide said alkylaromatics isomerization catalyst that comprises from 1 to 9 wt % ZSM-12 zeolite and more than 50wt % alumina binder, based on the total weight of said alkylaromatics isomerization catalyst;
wherein the alkylaromatics isomerization catalyst provides an ethylbenzene conversion of at least 37% wt at a PXate of 95 wt %.
16. A process as claimed in claim 15 in which the base is a compound according to the formula (R 1 R 2 R 3 NH)OH in which the compounds R 1 , R 2 , R 3 each independently are chosen from the group consisting of hydrogen and alkyl containing of from 1 to 6 carbon atoms.
17. A process as claimed in claim 16 in which a silica to alumina molar ratio of the ZSM-12 zeolite is in the range of from 60 to 200.
18. A process as claimed in claim 17 , wherein the anionic platinum complex is platinum chloride complex, and wherein the platinum chloride complex is hexachloroplatinic acid.
19. A process as claimed in claim 18 , wherein the alumina binder is present in carrier in an amount of more than 80 wt %.
20. A process as claimed in claim 19 , wherein the alkylaromatics isomerization catalyst comprises from 1 to 7 wt % of the ZSM-12 zeolite.
21. A process as claimed in claim 20 , wherein the alumina binder further comprises an additional compound selected from the group consisting of silica, titania, zirconia, ceria and gallia.
22. A process as claimed in claim 21 , wherein the alumina binder contains up to 10% wt of the additional compound.