Printer-compatible, pre-embossed films
Decorative films, useful for making a wide range of decorative laminates, that have a relatively deep texture on one major face and a relatively smoother, print receptive surface on the other major face. Notwithstanding the deep texture, the films have superb tracking characteristics and are compatible with a wide variety of automated printing operations. This allows automated printing equipment to print information directly onto the films.
1. A method of making a textured, decorative film, comprising the steps of:
a) extruding a molten film, wherein the film comprises polyvinyl chloride;
b) while the extruded film is at least partially molten, causing the film to pass through a gap between and contact first and second tooling surfaces that are maintained at one or more temperatures below the melt temperature of the molten film in a manner effective to help cause the molten film to set and solidify as the film passes through the gap, said first tooling surface comprising a plurality of depressions on the first tooling surface that provide cavities that are at least partially filled by the molten film as the film passes over the first tooling surface and sets, wherein said plurality of depressions have a plurality of different shapes and a plurality of different dimensions, wherein said plurality of different shapes comprise at least circular shaped depressions, and wherein said plurality of depressions are randomly arranged on the first tooling surface, and wherein said second tooling surface being relatively smoother than the first tooling surface, whereby a solidified film is formed comprising a first, textured major face having an Ra surface roughness of greater than about 100 microinches and a second, print receptive major face having an Ra surface roughness of less than 100 microinches, wherein the ratio of the Ra surface roughness of the first major face of the film to the Ra surface roughness of the second major face of the film is in the range from about 1.1:1 to about 500:1; and
c) printing decorative information onto the second major face of the film.
2. The method of claim 1 , wherein the film comprises less than 2 parts by weight of total plasticizer per 100 parts by weight of the film.
3. The method of claim 1 , wherein the film comprises less than 0.1 parts by weight of total plasticizer per 100 parts by weight of the film.
4. The method of claim 1 , wherein at least a portion of the depressions comprises generally flat bottoms.
5. The method of claim 1 , wherein the second tooling surface is biased toward the first tooling surface under pressure.
6. The method of claim 1 , wherein said plurality of different shapes further comprise oblong shaped depressions.
7. The method of claim 1 , wherein the plurality of depressions cover at least 50% of the first tooling surface.
8. The method of claim 1 , wherein the first tool surface includes a secondary texture formed at least on the depressions.
9. The method of claim 1 , wherein the depressions are formed over at least 98% of the first tooling surface that contacts the film.
10. The method of claim 1 , wherein the first, textured major face has an Ra surface roughness of at least 120 microinches.
11. The method of claim 1 , wherein the first, textured major face has an Ra surface roughness of at least 150 microinches.
12. The method of claim 1 , wherein the first major face has an Ra surface roughness of 160 to 190 microinches.
13. The method of claim 1 , wherein the first, textured major face has an Ra surface roughness of 120 to 300 microinches.
14. The method of claim 1 , wherein the second, print receptive major face has an Ra surface roughness in the range from 60 microinches to 90 microinches.
15. The method of claim 1 , wherein the second, print receptive major face has an Ra surface roughness of less than 60 microinches.
16. The method of claim 1 , wherein the ratio of the Ra surface roughness of the first, textured major face to the second, print receptive major face is in the range from about 3:2 to about 10:1.
17. The method of claim 1 , wherein the ratio of the Ra surface roughness of the first, textured major face to the second, print receptive major face is in the range from about 3:2 to about 3:1.
18. A method of making a decorative laminate, comprising;
a) providing a decorative film prepared according to the method of claim 1 ;
b) directly or indirectly bonding the film to a substrate.
19. A method of making a decorative film, comprising the steps of:
a) extruding a film having first and second major surfaces, wherein the film comprises polyvinyl chloride, wherein a pattern of protuberances is formed on the first major surface while the film is at least partially molten, wherein said protuberances have a plurality of different shapes and a plurality of different dimensions, wherein said plurality of different shapes comprise at least circular shaped protuberances, and wherein said protuberances are randomly arranged on the first major surface; and
b) after forming said pattern on the first major surface, printing decorative information onto the second major surface of the film.