Nitrile rubber article having natural rubber characteristics
View Patent ↗An carboxylated nitrile-butadiene rubber latex formulation composed of a blend of a first acrylonitrile terpolymer and a second acrylonitrile terpolymer, wherein: the acrylonitrile content of the blended terpolymers is between 17 and 45% by weight, the methacrylic acid content of the blended terpolymers is less than 15% by weight, and the remaining balance of the terpolymers being butadiene. The invention also includes an elastomeric nitrile rubber article made from the formulation.
1. An elastomeric glove formed from a carboxylated nitrile-butadiene rubber latex formulation comprising an acrylonitrile terpolymer, wherein:
the formulation has an acrylonitrile content between 17 and 45% by weight, a methacrylic acid content of less than 15% by weight, and wherein the remainder of the formulation contains butadiene, wherein the formulation further includes, in terms of parts per 100 dry parts of rubber consisting of the random terpolymer:
0-1.5 parts alkali hydroxide,
0.5-1.5 parts zinc oxide or other metal oxide,
0.5-1.5 parts sulfur, and
0.5-1.5 parts rubber accelerator,
wherein the glove has a palm thickness between 0.05 and 0.10 mm, a tensile strength at break of 30 MPa to 55 MPa, and an elongation at break of about 550-750%.
2. The elastomeric glove of claim 1 , wherein the glove has a thickness between 0.06 and 0.10 mm.
3. The elastomeric glove of claim 1 , wherein the glove has a thickness between 0.08 and 0.10 mm and a force at break of 8.7-10.2 N.
4. The elastomeric glove of claim 3 , wherein the glove has a force at break of 9.1-9.85 N.
5. The elastomeric glove of claim 3 , wherein the glove has a force at break of 9.18-9.5 N.
6. The elastomeric glove of claim 1 , wherein the thickness for the glove to have a force at break of 10.1 N is from 0.067 to 0.097 mm.
7. The elastomeric glove of claim 1 , wherein the glove has a thickness between 0.06 and 0.10 mm.
8. The elastomeric glove of claim 1 , wherein the glove has a thickness between 0.08 and 0.10 mm and a force at break of 8.7-10.2 N.
9. The elastomeric glove of claim 3 , wherein the glove has a force at break of 9.1-9.85 N.
10. The elastomeric glove of claim 3 , wherein the glove has a force at break of 9.18-9.5 N.
11. The elastomeric glove of claim 1 , wherein the thickness for the glove to have a force at break of 10.1 N is from 0.067 to 0.097 mm.
12. An elastomeric glove comprising a carboxylated nitrile-butadiene rubber formed from formulation containing an acrylonitrile terpolymer comprising a random terpolymer of acrylonitrile, butadiene and carboxylic acid, the terpolymer having an acrylonitrile content between 1 and 45% by weight, a carboxylic acid content up to about 15% by weight, and remaining balance of the terpolymer being butadiene, and the formulation further includes, in terms of parts per 100 dry parts of rubber consisting of the random terpolymer, 0-1.5 parts of an alkali agent that provides monovalent ions and 0.5-1.5 parts of a metallic oxide wherein the total combined amount of the alkali agent and metallic oxide is greater than 1.0 part per 100 dry parts of the rubber, 0.5-1.5 parts sulfur per 100 dry parts of the rubber, and 0.5-1.5 parts rubber accelerator per 100 dry parts of the rubber, wherein the glove has a palm thickness between 0.05 and 0.10 mm, a tensile strength at break of 30 MPa to 55 MPa, and an elongation at break of about 550-750%.
13. The elastomeric glove of claim 12 , wherein the alkali agent is selected from potassium hydroxide and ammonium hydroxide.
14. The elastomeric glove of claim 12 , wherein the rubber accelerator comprises a rubber accelerator selected from the group consisting of zinc diethyldithiocarbamate (ZDEC), zinc 2-mercaptobenzithiazole (ZMBT), and diphenyl guanidine (DPG).
15. An elastomeric glove comprising a carboxylated nitrile-butadiene rubber formed from formulation containing an acrylonitrile terpolymer comprising a random terpolymer of acrylonitrile, butadiene and carboxylic acid, the terpolymer having an acrylonitrile content between 17 and 45% by weight, a carboxylic acid content up to about 15% by weight, and remaining balance of the terpolymer being butadiene, and the formulation further includes, in terms of parts per 100 dry parts of rubber consisting of the random terpolymer, 0-1.5 parts of an alkali agent that provides monovalent ions and 0.5-1.5 parts of a metallic oxide wherein the total combined amount of the alkali agent and metallic oxide is greater than 1.0 part per 100 dry parts of the rubber, wherein the glove has a palm thickness between 0.05 and 0.10 mm, an elongation at break of about 550-750%, and wherein the thickness for the glove to have a force at break of 10.1 N is from 0.067 to 0.097 mm.