Method for optimizing the efficiency of wind turbine blades
View Patent ↗Method for protecting the surface of wind turbine blades manufactured with composites so as to furnish them with a finish resistant to normally-encountered external agents, namely rain, ice and grime from atmospheric pollution; and comprising one step for surface preparation as well as two steps for primer application and a second coating having a specified thickness.
1. A method for protecting the surface of a wind turbine blade manufactured with composites by preventing aerodynamic profile modifications during its useful life that would consequently impair its level of performance, comprising steps of:
a) sanding down an area on a leading edge of the blade intended for protection until its capacity of adherence attains a given level in relation with at least one of the following properties: glossiness, roughness, and surface tension;
b) applying a first coating onto said area, comprising a two-component compound primer of a polyurethane nature and a thickness range falling within 400-600 μm; and
c) applying a second coating to said area, comprising a two-component paint with a content of solids comprising 70-80%, including a base of aliphatic polyols as a binding agent and aliphatic polyisocyanate as a curing agent in a given proportion of 70-80% and 30-20% of its mass respectively, and a thickness range falling within 200-250,
wherein the second coating further comprises nanoparticles of hydrophilic silicon oxides and fluorinated polyhedral oligomeric silsesquioxanes.
2. The surface protection method according to claim 1 , wherein the width of said area on the leading edge of the blade is less than 40 mm.
3. The surface protection method according to claim 1 , further comprising steps of:
a) sanding down the rest of the blade surface until its capacity of adherence attains a given level in relation with at least one of the following properties: glossiness, roughness, and surface tension;
b) applying a first coating to the rest of the blade surface, comprising a two-component compound primer of a polyurethane nature and a thickness range falling within 300-500 μm; and
c) applying a second coating to the rest of the blade surface, comprising a two-component paint with a content of solids comprising 70-80%, including a base of aliphatic polyols as a binding agent and aliphatic polyisocyanate as a curing agent in a given proportion of 70-80% and 30-20% of its mass respectively, and a thickness range falling within 150-200 μm.
4. The surface protection method according to claim 1 , wherein the composite is glass fiber reinforced epoxy resin.
5. The surface protection method according to claim 1 , wherein the blade surface area intended for protection is sanded down until its glossiness is less than 5%.
6. The surface protection method according to claim 5 , wherein the blade surface area intended for protection is sanded down until its surface tension falls within the range of 30-35 mN/m.
7. The surface protection method according to claim 1 , wherein the second coating is formed by combining the two-component paint with a solution of the nanoparticles, wherein the solution of the nanoparticles comprises 5-10% of the mass of the second coating, and wherein the nanoparticles comprise 10-30% of the mass of the solution.