Hard-facing alloys having improved crack resistance
View Patent ↗Weld deposit compositions with improved crack resistance, improved wear resistance, and improved hardness are provided by controlling matrix grain size and balancing Titanium and/or Niobium with Carbon and/or Boron content. Additionally, the presence of coarse chromium carbides is drastically decreased to reduce the amount of check-cracking. Preferably, the weld deposit is produced from a flux-cored or metal-cored wire. The weld deposit characteristics include a matrix having a fine grain size, small evenly dispersed carbides within the matrix, and a small amount of Carbon in the matrix.
1. A weld deposit composition produced from a flux-cored or metal cored welding wire comprising, by percent mass:
between approximately 0.7% and approximately 2.0% Carbon;
between approximately 0.2% and approximately 0.5% Manganese;
between approximately 0.5% and approximately 1.1% Silicon;
between approximately 2.0% and approximately 8.0% Chromium;
between approximately 2.0% and approximately 6.0% Molybdenum;
between approximately 2.0% and approximately 5.0% Tungsten;
between approximately 2.0% and approximately 8.0% a sum of Niobium and Titanium;
between approximately 1.0% and approximately 2.5% Vanadium;
between approximately 0.2% and approximately 0.9% Boron; and
a balance of Iron,
wherein amounts of Titanium and Niobium are balanced with amounts of Carbon and Boron to form intermetallic carbides and borides that act as grain refiners, the ratio of Titanium or Niobium to Boron being about 4.4 for Titanium Boride, about 2.2 for Titanium Diboride, about 8.6 for Niobium Boride, and about 4.3 for Niobium Diboride.
2. The weld deposit composition according to claim 1 , wherein the Carbon comprises approximately 1.1%.
3. The weld deposit composition according to claim 1 , wherein the Manganese comprises approximately 0.3%.
4. The weld deposit composition according to claim 1 , wherein the Silicon comprises approximately 0.8%.
5. The weld deposit composition according to claim 1 , wherein the Chromium comprises approximately 4.0%.
6. The weld deposit composition according to claim 1 , wherein the Molybdenum comprises approximately 4.0%.
7. The weld deposit composition according to claim 1 , wherein the Tungsten comprises approximately 3.5%.
8. The weld deposit composition according to claim 1 , wherein the sum of Niobium and Titanium comprises approximately 3.2%.
9. The weld deposit composition according to claim 1 , wherein the Vanadium comprises approximately 1.8%.
10. The weld deposit composition according to claim 1 , wherein the Boron comprises approximately 0.5%.
11. The weld deposit composition according to claim 1 , wherein amounts of the Titanium and the Niobium are balanced with amounts of the Carbon and the Boron to reduce an amount of the Carbon and the Boron in a matrix and grain boundaries of the weld deposit composition.
12. The weld deposit composition according to claim 1 , further comprising carbides that are evenly dispersed within a matrix of the weld deposit composition.
13. The weld deposit composition according to claim 1 , wherein the weld deposit composition exhibits a fine grain size within a matrix thereof, combined with small and evenly dispersed carbides.
14. The weld deposit composition according to claim 1 , wherein carbides within the weld deposit composition have a size less than 0.1 mm.
15. The weld deposit composition according to claim 1 , wherein chromium carbides within the weld deposit composition have a size less than 0.1 mm.
16. The weld deposit composition according to claim 1 , wherein a matrix of the weld deposit composition has grains with a grain size less than 0.1 mm.
17. The weld deposit composition according to claim 1 , wherein the weld deposit composition has a hardness value of 63 to 65 HRC.
18. A flux-cored welding wire capable of producing a weld deposit composition comprising, by percent mass:
between approximately 0.7% and approximately 2.0% Carbon;
between approximately 0.2% and approximately 0.5% Manganese;
between approximately 0.5% and approximately 1.1% Silicon;
between approximately 2.0% and approximately 8.0% Chromium;
between approximately 2.0% and approximately 6.0% Molybdenum;
between approximately 2.0% and approximately 5.0% Tungsten;
between approximately 2.0% and approximately 8.0% a sum of Niobium and
Titanium;
between approximately 1.0% and approximately 2.5% Vanadium;
between approximately 0.2% and approximately 0.9% Boron; and
a balance of Iron,
wherein amounts of Titanium and Niobium are balanced with amounts of Carbon and Boron to form intermetallic carbides and borides that act as grain refiners, the ratio of Titanium or Niobium to Boron being about 4.4 for Titanium Boride, about 2.2 for Titanium Diboride, about 8.6 for Niobium Boride, and about 4.3 for Niobium Diboride.
19. A welded structure comprising at least one weld deposit, the weld deposit having a composition comprising, by percent mass:
between approximately 0.7% and approximately 2.0% Carbon;
between approximately 0.2% and approximately 0.5% Manganese;
between approximately 0.5% and approximately 1.1% Silicon;
between approximately 2.0% and approximately 8.0% Chromium;
between approximately 2.0% and approximately 6.0% Molybdenum;
between approximately 2.0% and approximately 5.0% Tungsten;
between approximately 2.0% and approximately 8.0% sum of Niobium and
Titanium;
between approximately 1.0% and approximately 2.5% Vanadium;
between approximately 0.2% and approximately 0.9% Boron; and
a balance of Iron,
wherein amounts of Titanium and Niobium are balanced with amounts of Carbon and Boron to form intermetallic carbides and borides that act as grain refiners; the ratio of Titanium or Niobium to Boron being about 4.4 for Titanium Boride, about 2.2 for Titanium Diboride, about 8.6 for Niobium Boride, and about 4.3 for Niobium Diboride.