Pasted zinc electrode for rechargeable nickel-zinc batteries
View Patent ↗Active material for a negative electrode of a rechargeable zinc alkaline electrochemical cell is made with zinc metal particles coated with tin and/or lead. The zinc particles may be coated by adding lead and tin salts to a slurry containing zinc particles, a thickening agent and water. The remaining zinc electrode constituents such as zinc oxide (ZnO), bismuth oxide (Bi 2 O 3 ), a dispersing agent, and a binding agent such as Teflon are then added. The resulting slurry/paste has a stable viscosity and is easy to work with during manufacture of the zinc electrode. Further, the zinc electrode is much less prone to gassing when cobalt is present in the electrolyte. Cells manufactured from electrodes produced in accordance with this invention exhibit much less hydrogen gassing, by as much as 60-80%, than conventional cells. The cycle life and shelf life of the cells is also enhanced, as the zinc conductive matrix remains intact and shelf discharge is reduced.
1. A method of making a zinc negative electrode, the method comprising:
(a) forming a coating consisting essentially of tin on zinc alloy particles;
(b) forming a paste comprising the coated zinc alloy particles, zinc oxide, bismuth oxide, and a binding agent; and
(c) incorporating the paste into a zinc electrode, wherein the tin comprises less than about 1% by weight of the paste and, wherein the zinc alloy particles comprise an alloy of zinc with an alloying element selected from the group consisting of bismuth, indium, and combinations thereof, and wherein the zinc alloy particles are less than about 100 micrometers in size.
2. The method of claim 1 , wherein the coating operation (a) comprises:
contacting the zinc alloy particles with a solution comprising at least one soluble tin salt.
3. The method of claim 1 , further comprising adding a pre-dissolved tin salt solution into the paste.
4. The method of claim 1 , wherein coating tin onto the zinc alloy particles comprises contacting the zinc alloy particles with a solution comprising at least one soluble tin salt selected from the group consisting of tin sulfate, tin acetate, tin chloride, tin fluoborate, and tin nitrate.
5. The method of claim 1 , wherein the paste further comprises dissolved tin salt.
6. The method of claim 1 , wherein the zinc alloy particles are less than about 40 microns in size.
7. A method of making a zinc negative electrode, the method comprising:
(a) forming a coating consisting essentially of lead on zinc alloy particles;
(b) forming a paste comprising the coated zinc alloy particles, zinc oxide, bismuth oxide, and a binding agent; and
(c) incorporating the paste into a zinc electrode, wherein the lead comprises less than about 0.05% by weight of the paste and wherein the zinc alloy particles comprise an alloy of zinc with an alloying element selected from the group consisting of bismuth, indium, and combinations thereof, and wherein the zinc alloy particles are less than about 100 micrometers in size.
8. The method of claim 7 , wherein coating lead onto the zinc alloy particles comprises contacting the zinc alloy particles with a solution comprising at least one soluble lead salt selected from the group consisting of lead acetate, lead chloride, lead fluoborate, and lead nitrate.
9. The method of claim 7 , wherein the zinc alloy particles are less than about 40 microns in size.
10. A method of making a zinc negative electrode, the method comprising:
(a) forming a coating consisting essentially of tin and lead on zinc alloy particles;
(b) forming a paste comprising the coated zinc alloy particles, zinc oxide, bismuth oxide, and a binding agent; and
(c) incorporating the paste into a zinc electrode, wherein the tin comprises less than about 1% by weight of the paste and lead comprises less than about 0.05% by weight of the paste, and, wherein the zinc alloy particles comprise an alloy of zinc with an alloying element selected from the group consisting of bismuth, indium, and combinations thereof, and wherein the zinc alloy particles are less than about 100 micrometers in size.
11. The method of claim 10 , wherein the coating operation (a) comprises:
contacting the zinc alloy particles with a solution comprising at least one soluble tin salt.
12. The method of claim 10 , further comprising adding a pre-dissolved tin salt solution into the paste.
13. The method of claim 10 , wherein coating tin onto the zinc alloy particles comprises contacting the zinc alloy particles with a solution comprising at least one soluble tin salt selected from the group consisting of tin sulfate, tin acetate, tin chloride, tin fluoborate, and tin nitrate.
14. The method of claim 10 , wherein coating lead onto the zinc alloy particles comprises contacting the zinc alloy particles with a solution comprising at least one soluble lead salt selected from the group consisting of lead acetate, lead chloride, lead fluoborate, and lead nitrate.
15. The method of claim 10 , wherein the paste further comprises dissolved tin salt.
16. The method of claim 10 , wherein the zinc alloy particles are less than about 40 microns in size.
17. A method of making a rechargeable nickel zinc cell, the method comprising:
(a) forming a negative zinc electrode comprising zinc powder particles, wherein said zinc powder particles are less than about 100 microns in size and are coated with a coating consisting essentially of tin, wherein the tin comprises less than about 1% by weight of the negative zinc electrode active material;
(b) forming a nickel positive electrode comprising a material selected from the group consisting of cobalt metal, cobalt compound, and combinations thereof; and
(c) incorporating the negative zinc electrode and the positive nickel electrode into the cell.
18. The method of claim 17 wherein the zinc powder particles are zinc alloy particles comprising an alloying element selected from the group consisting of bismuth and indium.
19. A method of making a rechargeable nickel zinc cell, the method comprising:
(a) forming a negative zinc electrode comprising zinc powder particles, wherein said zinc powder particles are less than about 100 microns in size and are coated with a coating consisting essentially of lead, wherein the lead comprises less than about 0.05% by weight of the negative zinc electrode active material;
(b) forming a nickel positive electrode comprising a material selected from the group consisting of cobalt metal, cobalt compound, and combinations thereof; and
(c) incorporating the negative zinc electrode and the positive nickel electrode into the cell.
20. A method of making a rechargeable nickel zinc cell, the method comprising:
(a) forming a negative zinc electrode comprising zinc powder particles, wherein said zinc powder particles are less than about 100 microns in size and are coated with a coating consisting essentially of tin and lead, wherein the tin comprises less than about 1% by weight of the negative zinc electrode active material and the lead comprises less than about 0.05% by weight of the negative zinc electrode active material;
(b) forming a nickel positive electrode comprising a material selected from the group consisting of cobalt metal, cobalt compound, and combinations thereof; and
(c) incorporating the negative zinc electrode and the positive nickel electrode into the cell.