TREATING WASTEWATER BY ULTRAFILTRATION IN FLUOROPOLYMER RESIN MANUFACTURE
The invention provides for a process for treating wastewater containing fluoropolymer resin waste solids comprising: passing the wastewater through hollow fiber membranes to separate fluoropolymer resin waste solids and produce treated filtrate water; and removing the fluoropolymer resin waste solids from the wastewater.
1 . A process for treating wastewater containing fluoropolymer resin waste solids comprising:
passing the wastewater through hollow fiber membranes to separate fluoropolymer resin waste solids and produce treated filtrate water; and
removing the fluoropolymer resin waste solids from the wastewater.
2 . The process of claim 1 wherein said wastewater is contained in a tank providing an upper exposed surface of the wastewater.
3 . The process of claim 2 wherein the fluoropolymer resin waste solids are removed from the surface of the wastewater.
4 . The process of claim 3 wherein fluoropolymer resin waste solids is removed by skimming the solids from the surface of the wastewater.
5 . The process of claim 1 wherein the treated filtrate water is substantially free of fluoropolymer resin.
6 . The process of claim 1 wherein the wastewater is passed through the hollow fiber membrane so that waste solids remains outside of the membrane and treated filtrate water flows through to the inside of the hollow fiber membrane.
7 . The process of claim 6 wherein air flow into the wastewater aids in moving the fluoropolymer waste solids from outside the membrane to the surface of the wastewater.
8 . The process of claim 1 wherein the passing of the wastewater through the hollow fiber membranes is assisted by lower pressure inside the hollow fiber membrane than outside.
9 . The process of claim 1 wherein the wastewater is passed through the membrane at a flow rate ranging from about 2 to about 45 l/m 2 ·hr.
10 . The process of claim 1 wherein the length of the hollow fibers range from about 1000 mm to about 2700 mm.
11 . The process of claim 1 wherein the pore size of the hollow fibers range from about 0.03 to about 0.07 μm.
12 . The process of claim 1 wherein the wastewater contains a surfactant which is passed through the hollow fiber membrane with the treated water filtrate.
13 . The process of claim 1 wherein the wastewater contains a fluoroether carboxylic acid or salt surfactant which is passed through the hollow fiber membrane with the treated water filtrate.
14 . The process of claim 13 wherein the treated water filtrate is concentrated to obtain a concentrated treated water filtrate.
15 . The process of claim 13 wherein the fluoroether carboxylic acid or salt surfactant is recovered from the treated water filtrate.
16 . The process of claim 1 wherein the fluoropolymer waste solids is periodically removed from the wastewater.
17 . The process of claim 14 wherein the treated water filtrate is concentrated by membrane separation.
18 . The process of claim 17 wherein the membrane separation is nanofiltration.