Separator membranes for lithium ion batteries and related methods
A battery separator for a secondary lithium battery includes a microporous/porous membrane with a ceramic coating of one or more layers, a layer may include one or more particles having an average particle size ranging from 0.01 μm to 5 μm and/or binders that include poly (sodium acrylate-acrylamide-acrylonitrile) copolymer.
1. A ceramic coated separator for an energy storage device, such as a secondary lithium ion battery, comprising:
a microporous polyolefin membrane having a first surface and a second surface, wherein said microporous membrane is at least one of a single layer, multiple layer, single ply, and/or multiple ply structure; and,
a ceramic coating on at least one surface of said microporous membrane, said ceramic coating comprising a layer of ceramic particles in a polymeric binder, said ceramic particles having an average particle size ranging from 0.01 μm to 5 μm in diameter, said polymeric binder includes poly (sodium acrylate-acrylamide-acrylonitrile) copolymer,
wherein said ceramic coated separator has a TMA TD shrinkage of about 0.5% or less at ≤130° C. and at least one of the following physical characteristics: a TMA MD dimensional change of −2% or more at ≤110° C.; a MD shrinkage of 15% or less at 135° C. for one hour; a volatile component evolution of ≥0.5% volatile components at ≥250° C.; and a strain shrinkage of 0% at ≥120° C.
2. The ceramic coated separator of claim 1 , wherein said ceramic particles comprise at least one of inorganic particles, ionically conductive materials, oxides of silicon (SiO 2 ), aluminum (Al 2 O 3 ), zirconium, titanium (TiO 2 ), mixtures thereof, or nitrides of silicon, aluminum, zirconium, calcium, or mixtures thereof, and/or mixtures, blends and/or combinations thereof.
3. The ceramic coated separator of claim 2 , wherein said ceramic particles comprise Al 2 O 3 .
4. The ceramic coated separator of claim 1 , wherein said ceramic coating on at least one surface of said microporous membrane has a thickness of about 1.5 μm to 5.5 um.
5. The ceramic coated separator of claim 1 , wherein said ceramic coated separator has a TMA MD dimensional change of −2% or more at ≤130° C.
6. The ceramic coated separator of claim 1 , wherein said ceramic coating on at least one surface of said microporous membrane has a thickness of about 3.0 μm to 5.5 μm, and said MD shrinkage is 28% or less at 150° C. for one hour.
7. The ceramic coated separator of claim 1 , wherein said microporous membrane is a wet process polyethylene microporous membrane, said ceramic coating on at least one surface of said microporous membrane has a thickness of about 3.0 μm to 5.5 μm, and said ceramic coated separator has an MD shrinkage of 2% or less at 135° C. for one hour.
8. The ceramic coated separator of claim 1 , wherein said ceramic coating on at least one surface of said microporous membrane has a thickness of about 3.0 μm to 5.5 μm, and said ceramic coated separator has a reduction in MD shrinkage at 135° C. for one hour of at least 40% over an uncoated membrane.
9. The ceramic coated separator of claim 1 , wherein said microporous membrane is a wet process polyethylene microporous membrane, said ceramic coating on at least one surface of said microporous membrane has a thickness of about 3.0 μm to 5.5 μm, and said ceramic coated separator has a reduction in MD shrinkage at 135° C. for one hour of at least 10% over an uncoated membrane.
10. The ceramic coated separator of claim 1 , wherein said ceramic coating on at least one surface of said microporous membrane has a thickness of about 5.5 μm to 9.0 μm, and said ceramic coated separator has an MD shrinkage of 4% or less at 135° C. for one hour.
11. The ceramic coated separator of claim 1 , wherein said microporous membrane is a wet process polyethylene microporous membrane, said ceramic coating on at least one surface of said microporous membrane has a thickness of about 5.5 μm to 9.0 μm, and said ceramic coated separator has an MD shrinkage of 2% or less at 135° C. for one hour.
12. The ceramic coated separator of claim 1 , wherein said ceramic coating on at least one surface of said microporous membrane has a thickness of about 5.5 μm to 9.0 μm, and said ceramic coated separator has a reduction in MD shrinkage at 135° C. for one hour of at least 80% over an uncoated membrane.
13. The ceramic coated separator of claim 1 , wherein said microporous membrane is a wet process polyethylene microporous membrane, said ceramic coating on at least one surface of said microporous membrane has a thickness of about 5.5 μm to 9.0 μm, and said ceramic coated separator has a reduction in MD shrinkage at 135° C. for one hour of at least 90% over an uncoated membrane.
14. The ceramic coated separator of claim 1 , wherein said ceramic coated separator has an aqueous binder and a scavenging filler, and said volatile component evolution is ≥1.0% volatile components at ≥250° C.
15. The ceramic coated separator of claim 1 , wherein said strain shrinkage of 0% is at ≥130° C.
16. The ceramic coated separator of claim 1 , wherein said microporous membrane is a polyolefinic microporous membrane and has an MD stretch of less than 20% at ≥120° C.
17. The ceramic coated separator of claim 1 , wherein said ceramic coating on at least one surface of said microporous membrane is a porous coating.
18. A secondary lithium ion battery comprises the ceramic coated separator of claim 1 .
19. An electric vehicle drive system comprises the secondary lithium ion battery of claim 18 .
20. The ceramic coated separator of claim 1 wherein said ceramic coating further comprises polyvinyl alcohol (PVOH), polyvinyl acetate (PVAc), polyacrylic acid salt, polyacrylonitrile, or copolymers thereof.