Processes for coating substrates and substrates formed therefrom
View Patent ↗Processes for coating substrates and the related substrates are disclosed herein. A one-component base coating composition is applied onto a substrate and a one-component top coating composition is applied wet-on-wet onto the applied base coating composition. The coating compositions are based on aqueous acrylate/polyurethane dispersions. The top coating composition is applied after the applied base coating composition develops a pendulum hardness of at least 50% of the pendulum hardness that would be exhibited by the base coating composition after UV cure. The applied coatings exposed to UV radiation to simultaneously cure both the base coating composition and the top coating composition.
1. A process for coating a substrate, comprising:
applying a one-component waterborne base coating composition onto a substrate, the base coating composition comprising a first aqueous epoxy acrylate/polyurethane dispersion;
applying a one-component waterborne top coating composition wet-on-wet onto the applied base coating composition after the applied base coating composition develops a pendulum hardness of at least 50% of a pendulum hardness that would be exhibited by the base coating composition after UV cure, the top coating composition comprising a mixture of a second aqueous epoxy acrylate/polyurethane dispersion and an aqueous polyester acrylate/polyurethane dispersion; and
exposing the applied coating compositions to UV radiation to simultaneously cure both the base coating composition and the top coating composition;
wherein the first aqueous epoxy aqueous acrylate/polyurethane dispersion may be the same or different than the second aqueous epoxy acrylate/polyurethane dispersion.
2. The process of claim 1 , wherein the applied base coating composition develops a pendulum hardness of at least 50% of the pendulum hardness that would be exhibited by the base coating composition after UV cure within 60 minutes physical dry time.
3. The process of claim 1 , wherein the applied coating compositions are exposed to UV radiation after the applied top coating composition exhibits a pendulum hardness of at least 50% of a pendulum hardness that would be exhibited by the top coating composition after UV cure.
4. The process of claim 3 , wherein the applied top coating composition develops a pendulum hardness of at least 50% of the pendulum hardness that would be exhibited by the top coating composition after UV cure within 60 minutes physical dry time.
5. The process of claim 1 , wherein the applied base coating composition develops a pendulum hardness of at least 40% of the pendulum hardness that would be exhibited by the base coating composition after UV cure within 30 minutes physical dry time.
6. The process of claim 1 , wherein the applied base coating composition develops a pendulum hardness of at least 40 seconds within 65 minutes physical dry time.
7. The process of claim 1 , wherein the applied base coating composition develops a pendulum hardness of at least 39 seconds within 60 minutes physical dry time.
8. The process of claim 1 , wherein the applied base coating composition develops a pendulum hardness of at least 30 seconds within 30 minutes physical dry time.
9. The process of claim 1 , wherein the applied top coating composition develops a pendulum hardness of at least 40 seconds within 65 minutes physical dry time.
10. The process of claim 1 , wherein the total elapsed time from application of the base coating composition to development of a dual-layer UV-cured coating is less than 3 hours.
11. The process of claim 1 , wherein the base coating composition is a pigmented composition and the top coating composition is a clearcoat composition.
12. The process of claim 1 , wherein the base coating composition and the top coating composition are both clearcoat compositions.
13. The process of claim 1 , wherein the first aqueous epoxy acrylate/polyurethane dispersion and second aqueous epoxy acrylate/polyurethane dispersion comprise a reaction product of components comprising:
A1) one or more unsaturated hydroxy-functional epoxy acrylate polymers;
B1) one or more dispersant compounds containing ionic groups, potentially ionic groups, and/or hydrophilic ether groups and groups reactive towards isocyanate groups;
C1) optionally, one or more polyols;
D1) one or more polyisocyanates; and
E1) one or more polyamines.
14. The process of claim 1 , wherein the aqueous polyester acrylate/polyurethane dispersion comprises a reaction product of components comprising:
A) one or more unsaturated hydroxy-functional polyester acrylate polymers;
B) one or more dispersant compounds containing ionic groups, potentially ionic groups, and/or hydrophihc ether groups and groups reactive towards isocyanate groups;
C) optionally, one or more polyols;
D) one or more polyisocyanates; and
E) one or more polyamines.
15. The process of claim 1 , wherein the substrate comprises a material selected from the group consisting of concrete, stone, brick, plastic, metal, and wood.
16. The process of claim 1 , wherein the substrate is a floor.
17. A process for coating a substrate, comprising:
applying a one-component waterborne base coating composition onto a substrate, the base coating composition comprising a first aqueous epoxy acrylate/polyurethane dispersion;
applying a one-component waterborne top coating composition wet-on-wet onto the applied base coating composition after the applied base coating composition develops a pendulum hardness of at least 35 seconds, the top coating composition comprising a mixture of a second aqueous epoxy acrylate/polyurethane dispersion and an aqueous polyester acrylate/polyurethane dispersion, and
exposing the applied coating compositions to UV radiation to simultaneously cure both the base coating composition and the top coating composition.
18. The process of claim 17 , wherein the applied base coating composition develops a pendulum hardness of at least 35 seconds within 60 minutes physical dry time.
19. The process of claim 17 , wherein the applied base coating composition develops a pendulum hardness of at least 39 seconds within 60 minutes physical dry time.
20. The process of claim 17 , wherein the applied base coating composition develops a pendulum hardness of at least 40 seconds within 65 minutes physical dry time.
21. The process of claim 17 , wherein the total elapsed time from application of the base coating composition to development of a dual-layer UV-cured coating is less than 3 hours.
22. The process of claim 17 , wherein the base coating composition is a pigmented composition and the top coating composition is a clearcoat composition.
23. The process of claim 17 , wherein the base coating composition and the top coating composition are both clearcoat compositions.
24. The process of claim 17 , wherein the first aqueous epoxy acrylate/polyurethane dispersion and second aqueous epoxy acrylate/polyurethane dispersion comprise a reaction product of components comprising:
A1) one or more unsaturated hydroxy-functional epoxy acrylate polymers;
B1) one or more dispersant compounds containing ionic groups, potentially ionic groups, and/or hydrophllic ether groups and groups reactive towards isocyanate groups;
C1) optionally, one or more polyols;
D1) one or more polyisocyanates; and
E1) one or more polyamines.
25. The process of claim 17 , wherein the aqueous polyester acrylate/polyurethane dispersion comprises a reaction product of components comprising:
A) one or more unsaturated hydroxy-functional polyester acrylate polymers;
B) one or more dispersant compounds containing ionic groups, potentially ionic groups, and/or hydrophilic ether groups and groups reactive towards isocyanate groups;
C) optionally, one or more polyols;
D) one or more polyisocyanates; and
E) one or more polyamines.
26. The process of claim 17 , wherein the substrate comprises a material selected from the group consisting of concrete, stone, brick, plastic, metal, and wood.
27. The process of claim 17 , wherein the substrate is a floor.