Method of making medical tubing having variable characteristics using thermal winding
View Patent ↗An efficient and cost-effective method of manufacturing a kink-resistant tube, wherein a coated wire is wound around a mandrel while simultaneously being heated to melt the coating, is provided.
1. A method for manufacturing a coated guidewire, comprising the steps of providing a core wire and winding a coated wire around core wire while simultaneously heating the coated wire, to thereby melt the coating around the two wires to form a coated guidewire, the core wire being used instead of a mandrel.
2. The method of claim 1 , further comprising the step of providing a hot air gun to apply heat to melt the coating.
3. The method of claim 1 , further comprising the step of providing a roller to smooth the surface of the melted coating along the guidewire.
4. The method of claim 3 , wherein the roller is heated.
5. The method of claim 1 further comprising the steps of:
providing a winding machine; and
adjusting the speed of the winding machine and heating temperature based on the material and diameter of the coated wire and the diameter of the core wire.
6. A method for manufacturing a coated guidewire, comprising the steps of:
placing a core wire between two spindles of a winding machine;
winding a co-extruded wire comprising a metal wire coated in a thermoplastic polymer around the core wire about three to four times;
attaching the end of the co-extruded wire to the spindle;
starting the winding machine and winding the co-extruded wire over the core wire while simultaneously applying heat to melt the thermoplastic polymer as it is wound around the core wire to melt the co-extruded wire to the core wire and thereby produce a coated guidewire;
when the winding is complete, cutting the co-extruded wire close to the core wire and removing the produced coated guidewire from the winding machine, the core wire is not removed from the produced coated guidewire.
7. The method of claim 6 , wherein a hot air gun is used to apply heat to melt the thermoplastic polymer.
8. The method of claim 6 , further comprising the step of providing a roller to smooth the surface of the melted thermoplastic polymer along the guidewire.
9. The method of claim 8 , wherein the roller is heated.
10. The method of claim 9 further comprising adjusting speed of the winding machine and temperatures of the hot air and heated roller being based on material and diameter of the co-extruded wire.
11. The method of claim 6 further comprising adjusting speed of the winding machine being based on material and diameter of the co-extruded wire.
12. The method of claim 6 further comprising adjusting temperatures of the hot air being based on material and diameter of the co-extruded wire.
13. The method of claim 9 further comprising adjusting temperatures of the heated roller being based on material and diameter of the co-extruded wire.