Powder coating compositions for low temperature curing and high flow
The present invention discloses powder coating compositions and to components and ingredients for incorporation therein, suitable for low temperature curing schedule and with excellent resistance to outside aging. The powder coating composition can be cured at a temperature from 140° C. to lead to a coating with excellent flow and high gloss. In one aspect of the invention, a composition having a polyester resin comprises 0.1 to 60 weight percent of mono or poly-functional satured or unsatured fatty acids of mixtures of them, 30 to 60 weight percent of an aromatic diacid or cycloalkyl diacids or anhydride 20 to 30 weight percent of aliphatic diol, 0 to 6 weight percent of aliphatic triol, 0 to 10 weight percent of isosorbide and isomers or cycloalkyl diol, 0 to 10 weight percent of C 3 -C 12 aliphatic diacid, and with total weight percent of the monomers equal to 100.
1. A powder coating composition comprising a polyester resin comprising:
(1) 0.1 to 60 weight percent of mono or poly-functional saturated or unsaturated fatty acids or mixtures thereof,
(2) 30 to 60 weight percent of an aromatic diacid or cycloalkyl diacids or anhydrides selected from the group consisting of isophthalic acid, terephthalic acid, phthalic anhydride, trimellitic anhydride, furandicarboxylic acid, cyclohexandicarboxilic acid, hexahydrophtalic anhydride, and combinations thereof,
(3) 20 to 30 weight percent of aliphatic diol,
(4) 0 to 6 weight percent of aliphatic triol,
(5) 5 to 10 weight percent of isosorbide and isomers of isosorbide,
(6) 0 to 10 weight percent of C 3 -C 12 aliphatic diacid, and
with total weight percent of the monomers equal to 100, wherein an acid/alcohol mole ratio is higher than 1 and with an acid value of higher than 15 mg KOH/g and wherein the polyester resin has a melt viscosity at 200° C. from 1500 to 12000 mPa·s and a Tg of above 44° C. and lower than 70° C.
2. The powder coating composition of claim 1 wherein the polyester resin comprises:
(1) 0.5 to 30 weight percent of mono or poly-functional saturated or unsaturated fatty acids of mixtures of them,
(2) 30 to 60 weight percent of an aromatic diacid or cycloalkyl diacid or anhydride,
(3) 20 to 30 weight percent of aliphatic diol,
(4) 0 to 6 weight percent of aliphatic triol,
(5) 5 to 10 weight percent of isosorbide and isomers of isosorbide,
(6) 0 to 10 weight percent of C 3 -C 12 aliphatic diacid, and
with total weight percent of the monomers equal to 100.
3. The powder coating composition of claim 1 further comprising a curative selected from the group consisting of a non-isocyanurate polyepoxide, beta-hydroxyalkylamide, triglycidyl-isocyanurate, and epoxy resins in a weight percent from 2.5 to 50 based on total weight of polyester resin and curative.
4. The powder coating composition of claim 3 wherein the epoxy resins are selected from the group consisting of glycidyl ethers of bisphenol A, glycidyl ethers of bisphenol F, epoxy novolac resins, glycidyl esters, and mixtures thereof.
5. The powder coating composition of claim 1 wherein the cure temperature is lower than 180° C. and higher than 100° C.
6. A coated article comprising the polymeric composition of claim 5 in a cured film.
7. The powder coating composition of claim 1 , wherein the polyester resin comprises:
(1) 8.5 weight percent of saturated dimer/trimer fatty acid;
(2) 34.9 weight percent of terephthalic acid;
(3) 18.2 weight percent of isophthalic acid;
(4) 30.3 weight percent of 90% neopentylglycol;
(5) 0.9 weight percent of trimethylolpropane;
(6) 2.1 weight percent adipic acid; and
(7) 5 weight percent of D-isosorbide.
8. The powder coating composition of claim 1 , wherein the polyester resin comprises:
(1) 8.4 weight percent of saturated dimer/trimer fatty acid;
(2) 35.7 weight percent of terephthalic acid;
(3) 18.6 weight percent of isophthalic acid;
(4) 30.7 weight percent of 90% neopentylglycol;
(5) 0.8 weight percent of trimethylolpropane; and
(6) 5.7 weight percent of D-isosorbide.