Closure and liner compositions essentially free of ethylene vinyl acetate copolymer
View Patent ↗The invention provides liner resin compositions which are essentially free of ethylene vinyl alcohol (EVA) copolymer and molded plastic closures which include the described liner resin compositions. Instead of EVA copolymers, the provided liner resin compositions generally include low density polyethylene (LDPE). Accordingly, in one embodiment, the invention provides a liner resin composition comprising: a) LDPE; b) metallocene-catalyzed very low density polyethylene; c) a random copolymer; and d) a lubricant; wherein said liner composition is essentially free of EVA copolymer.
1. A liner resin composition comprising:
a) between about 60% and about 70% of low density polyethylene (LDPE);
b) between about 10% and about 30% of metallocene-catalyzed very low density polyethylene;
c) between about 5% and about 10% of a random copolymer; and
d) about 1% of a lubricant;
wherein said liner resin composition is essentially free of ethylene vinyl acetate (EVA) copolymer; and wherein said amounts are based on the total weight of the liner resin composition.
2. The liner resin composition according to claim 1 further comprising a colorant.
3. The liner resin composition according to claim 1 , wherein said liner resin composition is essentially free of a mineral oil.
4. The liner resin composition according to claim 1 , wherein the random copolymer is a random polypropylene copolymer.
5. The liner resin composition according to claim 1 , wherein said lubricant is erucamide.
6. The liner resin composition according to claim 2 , wherein the amount of metallocene-catalyzed very low density polyethylene is between about 10% and about 30%; the amount of the random copolymer is between about 5% and about 10%; the amount of the lubricant is about 1%; the amount of the colorant is sufficient to achieve the desired color of the liner composition; and the amount of LDPE is between about 60% and about 70%, wherein said amounts are based on the total weight of the liner resin composition.
7. The liner resin composition according to claim 6 , wherein the amount of metallocene-catalyzed very low density polyethylene is about 20%.
8. The liner resin composition according to claim 6 , wherein the random copolymer is a random polypropylene copolymer.
9. The liner resin composition according to claim 8 , wherein the amount of the random polypropylene copolymer is about 8%.
10. The liner resin composition according to claim 6 , wherein the lubricant is erucamide.
11. The liner resin composition according to claim 1 , wherein the liner resin composition is a dry blend mixture of:
a) LDPE;
b) metallocene-catalyzed very low density polyethylene; and
c) a masterbatch, wherein said masterbatch comprises LDPE, the random copolymer, the lubricant, and, optionally, a colorant.
12. A finalized liner resin composition prepared from the liner resin composition according to claim 11 .
13. The finalized resin composition according to claim 12 , wherein the melt flow index of said finalized resin composition is between about 20 and about 25.
14. The liner resin composition according to claim 1 , wherein said liner resin composition is molded into a closure.
15. A molded closure comprising the liner resin composition according to claim 1 .