Steel for carburizing or carbonitriding use
View Patent ↗A steel for carburizing or carbonitriding use consisting of, by mass %, C: 0.1 to 0.3%, Si: 0.01 to 0.15%, Mn: 0.6 to 1.5%, S: 0.012 to 0.05%, Cr: 0.5 to 2.0%, Al: 0.030 to 0.050%, Ti: 0.0006 to 0.0025%, N: 0.010 to 0.025%, and O: 0.0006 to 0.0012%, and, optionally, at least one selected from Mo≤0.5%, Ni≤1.5% and Cu≤0.4%, and the balance of Fe and impurities. P and Nb are P≤0.025% and Nb≤0.003% respectively. Formulas of [−5.0≤log (Ti×N)≤−4.4] and [−12.5≤log (Al 2 ×O 3 )≤−11.7] are satisfied. Austenite grain coarsening is prevented even when the steel is heated in the process of carburizing or carbonitriding, and even under various hot forging temperatures. The steel has excellent bending fatigue strength after carburizing or carbonitriding.
1. A steel for carburizing or carbonitriding use consisting of, by mass %;
C: 0.18 to 0.3%,
Si: 0.01 to 0.09%,
Mn: 0.6 to 1.5%,
S: 0.012 to 0.05%,
Cr: 0.5 to 2.0%,
Al: 0.030 to 0.050%,
Ti: 0.0006 to 0.0025%,
N: 0.010 to 0.025%, and
O: 0.0006 to 0.0012%, and
the balance of Fe and impurities, wherein P and Nb among the impurities are P: 0.025% or less and Nb: 0.003% or less respectively,
and further the following formulas (1) and (2) are satisfied:
−5.0≤log(Ti×N)≤−4.4 (1),
−12.5≤log(Al 2 ×O 3 )≤−11.7 (2),
wherein each element symbol in the above formulas (1) and (2) represents the content by mass percent of the element concerned.
2. A steel for carburizing or carbonitriding use consisting of, by mass %;
C: 0.18 to 0.3%,
Si: 0.01 to 0.09%,
Mn: 0.6 to 1.5%,
S: 0.012 to 0.05%,
Cr: 0.5 to 2.0%,
Al: 0.030 to 0.050%,
Ti: 0.0006 to 0.0025%,
N: 0.010 to 0.025%,
O: 0.0006 to 0.0012%, and
at least one element selected from Mo: 0.5% or less, Ni: 1.5% or less, and Cu: 0.4% or less, and
the balance of Fe and impurities, wherein P and Nb among the impurities are P: 0.025% or less and Nb: 0.003% or less respectively,
and further the following formulas (1) and (2) are satisfied:
−5.0≤log(Ti×N)≤−4.4 (1),
−12.5≤log(Al 2 ×O 3 )≤−11.7 (2),
wherein each element symbol in the above formulas (1) and (2) represents the content by mass percent of the element concerned.
3. The steel for carburizing or carbonitriding use according to claim 1 , the steel has less than two austenite grains having a grain size number of 4 or less exist in the field of 10 mm 2 , when the steel is heated at 1050 to 1300° C., hot forged, cooled down to room temperature, and heated at 980° C. or less for three hours or less.
4. The steel for carburizing or carbonitriding use according to claim 1 , the steel has less than two austenite grains having a grain size number of 4 or less exist in the field of 10 mm 2 , when the steel is heated at 1050 to 1300° C., hot forged, cooled down to room temperature, and heated at 980° C. or less for three hours or less.