Electron-beam welded joint, steel for electron-beam welding, and manufacturing method
View Patent ↗An electron-beam welded joint including, by mass %, C: 0.02% to 0.1%, Si: 0.03% to 0.30%, Mn: 1.5% to 2.5%, Ti: 0.005 to 0.015%, N: 0.0020 to 0.0060%, O: 0.0010% to 0.0035%, Nb: 0% to 0.020%, V: 0% to 0.030%, Cr: 0% to 0.50%, Mo: 0% to 0.50%, Cu: 0% to 0.25%, Ni: 0% to 0.50%, B: 0% to 0.0030%, S: limited to 0.010% or less, P: limited to 0.015% or less, Al: limited to 0.004% or less, and a balance consisting of iron and unavoidable impurities, wherein an index value CeEB is 0.49% to 0.60%, a number of oxides having an equivalent circle diameter of 1.0 μm or more is 20 pieces/mm 2 or less, and a number of oxides having an equivalent circle diameter of 0.05 μm or more and less than 0.5 μm is 1×10 3 pieces/mm 2 to 1×10 5 pieces/mm 2 at a thickness center portion.
1. An electron-beam welded joint obtained by applying an electron-beam welding to a steel, the steel comprising as a composition, by mass %,
C: 0.02% to 0.10%,
Si: 0.03% to 0.30%,
Mn: 1.5% to 2.5%,
Ti: 0.005% to 0.015%,
N: 0.0020% to 0.0060%,
O: 0.0010% to 0.0035%
Nb: 0% to 0.020%,
V: 0% to 0.030%,
Cr: 0% to 0.50%,
Mo: 0% to 0.50%,
Cu: 0% to 0.25%,
Ni: 0% to 0.50%,
B: 0% to 0.0030%,
S: limited to 0.010% or less,
P: limited to 0.015% or less,
Al: limited to 0.004% or less, and
a balance consisting of iron and unavoidable impurities, wherein
an index value CeEB defined by a following Formula 1 is 0.49% to 0.60%,
a C/CeEB, which is a ratio of an amount in mass % of C in the steel relative to the index value CeEB of the steel, is 0.04 to 0.18,
a number of oxides having an equivalent circle diameter of 1.0 μm or more is 20 pieces/mm 2 or less at a thickness center portion in a cross-section along a thickness direction of the steel, and
a number of oxides containing Ti of 10% or more and having an equivalent circle diameter of 0.05 μm or more and less than 0.5 μm is 1×10 3 pieces/mm 2 to 1×10 5 pieces/mm 2 at the thickness center portion,
the index value of hardenability after the electron-beam welding, CeEB=C+(9/40)Mn+(1/15)Cu+(1/15)Ni+(1/5)Cr+(1/5)Mo+(1/5)V (Formula I)
where C, Mn, Cu, Ni, Cr, Mo and V represent amounts in mass % of each element contained in the composition of the steel.
2. The electron-beam welded joint according to claim 1 , wherein the steel has a thickness of 45 to 150 mm.
3. The electron-beam welded joint according to claim 1 , wherein, when a CTOD value of a welded metal is defined as δ WM , a CTOD value of a weld heat-affected zone is defined as δ HAZ , and a CTOD value of the steel is defined as δ BM ,
0.5≦δ WM /δ BM ≦1.1, and 0.5≦δ HAZ /δ BM ≦1.1 are satisfied.
4. A steel for an electron-beam welding, the steel comprising as a composition, by mass %,
C: 0.02% to 0.10%,
Si: 0.03% to 0.30%,
Mn: 1.5% to 2.5%,
Ti: 0.005% to 0.015%,
N: 0.0020% to 0.0060%,
O: 0.0010% to 0.0035%,
Nb: 0% to 0.020%,
V: 0% to 0.030%,
Cr: 0% to 0.50%,
Mo: 0% to 0.50%,
Cu: 0% to 0.25%,
Ni: 0% to 0.50%,
B: 0% to 0.0030%,
S: limited to 0.010% or less,
P: limited to 0.015% or less,
Al: limited to 0.004% or less, and
a balance consisting of iron and unavoidable impurities, wherein
an index value CeEB obtained by substituting the composition of the steel into a following Formula I is 0.49% to 0.60%,
a C/CeEB, which is a ratio of an amount in mass % of C in the steel relative to the index value CeEB of the steel, is 0.04 to 0.18,
a number of oxides having an equivalent circle diameter of 1.0 μm or more is 20 pieces/mm 2 or less at a thickness center portion in a cross-section along a thickness direction of the steel, and
a number of oxides containing Ti of 10% or more and having an equivalent circle diameter of 0.05 μm or more and less than 0.5 μm is 1×10 3 pieces/mm 2 to 1×10 5 pieces/mm 2 at the thickness center portion,
the index value of hardenability after electron-beam welding, CeEB=C+(9/40)Mn+(1/15)Cu+(1/15)Ni+(1/5)Cr+(1/5)Mo+(1/5)V (Formula I)
where C, Mn, Cu, Ni, Cr, Mo, and V represent amounts in mass % of each element contained in the composition of the steel.
5. The steel for the electron-beam welding according to claim 4 , wherein the steel has a thickness of 45 to 150 mm.
6. A method of manufacturing the steel for the electron-beam welding according to claim 4 , the method comprising,
a casting process of casting and cooling the steel so that a cooling rate in a temperature range of 1300° C. to 1100° C. is 9° C./min or more, and
a process of heating the steel to a temperature range of 950° C. to 1150° C. after the casting process, and thereafter thermomechanical-treating the steel.
7. A method of manufacturing the steel for the electron-beam welding according to claim 5 , the method comprising,
a casting process of casting and cooling the steel so that a cooling rate in a temperature range of 1300° C. to 1100° C. is 9° C./min or more, and
a process of heating the steel to a temperature range of 950° C. to 1150° C. after the casting process, and thereafter thermomechanical-treating the steel.