Polystyrene melt extrusion process
View Patent ↗Extruded polystyrene foams are made with an added brominated styrene-butadiene polymer as a flame retardant. The blowing agent is a mixture of carbon dioxide, ethanol and water, which may also contain a C 4 -C 5 hydrocarbon. The blowing agent mixture overcomes a tendency of the brominated styrene-butadiene to form very small cells. This allows the foam to expand fully to form good quality, low density extruded foam.
1. A process for making a polymer foam, comprising forming a pressurized melt that contains a molten styrenic polymer, a flame retarding amount of a brominated styrene-butadiene polymer and 1.1 to 1.70 moles of a blowing agent mixture per kilogram of the styrenic polymer, and forcing the melt through an opening into a zone the blowing agent expands and the polymer cools and solidifies to form a foam, wherein the blowing agent mixture includes 0.65 to about 0.9 moles of carbon dioxide per kilogram of the styrenic polymer, 0.25 to 0.45 moles of ethanol per kilogram of the styrenic polymer, 0.1 to 0.3 moles of a C 4 -C 5 hydrocarbon per kilogram of the styrenic polymer and 0.1 to 0.3 moles of water per kilogram of the styrenic polymer, wherein the average cell size of the foam is from 0.25 mm to 1 mm.
2. The process of claim 1 , wherein the C 4 -C 5 hydrocarbon is isobutene.
3. The process of claim 1 wherein the amount of blowing agent mixture is from 1.15 to 1.65 moles per kilogram of the styrenic polymer.
4. The process of claim 1 wherein the blowing agent mixture contains, per kilogram of the styrenic polymer, 0.65 to 0.9 moles of carbon dioxide, 0.25 to 0.45 moles of ethanol, 0.1 to 0.3 moles of isobutane and from 0.1 to 0.3 moles of water, with the total amount of blowing agent mixture being from 1.15 to 1.65 moles per kilogram of the styrenic polymer.
5. The process of claim 1 wherein the foam density is no greater than 36 kg/m 3 .
6. The process of claim 1 wherein the foam has an open cell content of no greater than 30%.
7. The process of claim 1 wherein the foam has a thickness of at least 12 mm.
8. The process of claim 1 wherein the foam has a thickness of at least 20 mm.
9. The process of claim 1 wherein the brominated styrene-butadiene polymer is a brominated block copolymer of styrene and butadiene which contains at least 50% by weight bromine.