Negative electrode material for lithium ion secondary batteries, and method for producing same
View Patent ↗A negative electrode material for lithium ion secondary batteries comprises amorphous coated particles that are composed of a plurality of consolidated particles having no specific shape, said consolidated particles being obtained by consolidating a plurality of primary spheroidized graphite particles, and 0.5-20% by mass of an amorphous carbon layer that covers the surfaces of the consolidated particles and binds the consolidated particles with each other; and 0.5-20% by mass of a highly crystalline carbon layer that is formed so as to cover the outer surfaces of the amorphous coated particles and has an interplanar distance ascribed to CVD processing of 0.335 nm or more but less than 0.3369 nm. The negative electrode material for lithium ion secondary batteries is also characterized by having a porosity of 5% by volume or less, and a method for producing the negative electrode material for lithium ion secondary batteries.
1. A negative electrode material for lithium ion secondary batteries comprising:
amorphous coated particles which are composed of a plurality of consolidated particles having no specific shape, obtained by consolidating a plurality of primary spheroidized graphite particles and 0.5 to 20% by mass of an amorphous carbon layer coating the surfaces of the consolidated particles and bonding the consolidated particles with each other, wherein the amorphous carbon layer has a thickness of 0.05 to 2 μm, and
0.5 to 25% by mass of a highly crystalline carbon layer having an interplanar spacing of 0.335 nm to less than 0.3369 nm, formed by a CVD so as to cover the outer surfaces of the amorphous coated particles,
and which is also characterized by having a porosity of 5% by volume or less.
2. The negative electrode material for lithium ion secondary batteries, set forth in claim 1 , wherein the porosity is 0.5 to 4.1% by volume.
3. The negative electrode material for lithium ion secondary batteries, set forth in claim 1 , which has a bulk density of 0.4 to 0.9 g/ml.
4. The negative electrode material for lithium ion secondary batteries, set forth in claim 1 , which has a tap density of 0.7 to 1.3 g/ml.
5. The negative electrode material for lithium ion secondary batteries, set forth in claim 1 , wherein the consolidated particles have an average particle diameter of 5 to 40 μm.
6. The negative electrode material for lithium ion secondary batteries, set forth in claim 1 , wherein the number of the consolidated particles is 3 to 50.
7. The negative electrode material for lithium ion secondary batteries, set forth in claim 1 , wherein the highly crystalline carbon layer has a thickness of 0.05 to 2 μm.
8. A method for producing a negative electrode material for lithium ion secondary batteries set forth in claim 1 , which comprising the following steps:
(1) a granulation step of subjecting a slurry containing primary spheroidized graphite particles of 5 to 40 μm in average particle diameter and a phenolic resin, to produce secondary particles of 10 to 200 μm in average particle diameter,
(2) a step of subjecting the secondary particles to pressure molding at 5 to 50 kN to produce a molded material of secondary particles,
(3) a disintegration step of disintegrating the molded material of secondary particles to obtain disintegrated particles of 10 to 50 μm in average particle diameter,
(4) a firing step of heating the disintegrated particles in an inert gas atmosphere at 800 to 1,500° C. for 0.5 to 10 hours to obtain fired particles, and
(5) a CVD step of subjecting the fired particles to a CVD in a fluidized bed to form highly crystalline carbon on the surfaces of the fired particles.
9. A negative electrode for lithium ion secondary batteries, which incorporates a negative electrode material for lithium ion secondary batteries set forth in claim 1 .
10. A lithium ion secondary battery which uses a negative electrode set forth in claim 9 .