Melt-blown nonwoven fabric, and production process and apparatus for the same
It is an object of the present invention to provide a stable production process for a melt-blown nonwoven fabric comprising thin fibers and having extremely few thick fibers [number of fusion-bonded fibers] formed by fusion bonding of thermoplastic resin fibers to one another, and an apparatus for the same. The present invention relates to a melt-blown nonwoven fabric comprising polyolefin fibers and having (i) a mean fiber diameter of not more than 2.0 μm, (ii) a fiber diameter distribution CV value of not more than 60%, and (iii) 15 or less fusion-bonded fibers based on 100 fibers; a production process for a melt-blown nonwoven fabric characterized by feeding cooling air of not higher than 30° C. from both side surfaces of outlets of slits 31 from which high-temperature high-velocity air is gushed out and thereby cooling the spun molten resin; and a production apparatus for the same.
1. A production process for a melt-blown nonwoven fabric, comprising spinning out a molten thermoplastic resin through a nozzle having a number of holes lined up, said holes having a diameter of 0.05 mm to 0.4 mm, said molten resin having been forcedly fed to a melt-blowing die, and accumulating fibers on a moving collection plate, said fibers being obtained by drawing and thinning the molten resin by air gushed out from slits provided so as to interpose a line of the holes therebetween, said air having a temperature not lower than 280° C. and a flow rate of 200 Nm 3 /hr/m to 1000 Nm 3 /hr/m, wherein:
a cooling fluid of not higher than 30° C. is horizontally fed along a nozzle surface from side surfaces of outlets of the slits from which the air is gushed out, and through an attachment to introduce the cooling fluid for cooling the spun thermoplastic resin fibers which has been mounted on the tip of the melt-blowing die without any space between the attachment and the tip of the melt-blowing die, to cool the spun thermoplastic resin fibers, said surfaces facing away from the line of the holes.
2. The production process for a melt-blown nonwoven fabric as claimed in claim 1 , wherein the cooling fluid is cooling air.
3. A production apparatus for a melt-blown nonwoven fabric, said apparatus comprising:
a melt-blowing die to which a molten resin is forcedly fed,
a nozzle having a number of holes lined up to said molten thermoplastic resin,
a moving collection plate to accumulate fibers,
slits provided so as to interpose a line of the holes therebetween and from which air is gushed out to draw and thin the molten resin to obtain said fibers, and
an attachment removably mounted on the tip of the melt-blowing die along a nozzle surface without any space between the attachment and the tip of the melt-blowing die, to introduce a cooling fluid for cooling the spun thermoplastic resin fibers.