Method for separating nickel from material with low nickel content
View Patent ↗The invention relates to a method for separating nickel and other valuable metals particularly from material having low nickel content, which contains iron and magnesium in addition to nickel and other valuable metals. The material having low nickel content is subjected to pulping and atmospheric leaching in acidic and oxidizing conditions, in which the majority of the metals in the material dissolve and the iron is partially precipitated. The precipitated iron is separated from the solution, after which nickel and the other dissolved valuable metals are precipitated as sulphides.
1. A method for separating nickel and other valuable metals from nickel-poor iron-containing material generated in a nickel ore concentration process, which method comprises
a) a pulping stage, wherein the nickel-poor material is pulped into an acid-containing leaching solution, and the pH of the leaching solution is adjusted to a range of 1.5-3.0,
b) an atmospheric leaching stage, wherein the nickel-poor material obtained from the pulping stage is contacted with an acid-containing solution and an oxygen-containing gas.
2. The method according to claim 1 , wherein after pulping of the nickel-poor material in the pulping stage, the material is routed to atmospheric leaching in which a second part of the nickel, the other valuable metals and iron are leached by means of an acid-containing solution and an oxygen-containing gas and in which a first part of the iron is precipitated during the atmospheric leaching stage, after which the precipitated iron is separated from the valuable metal-containing acid solution and the valuable metal-containing solution is routed to precipitation of nickel and other valuable metals, which is performed by sulphide precipitation.
3. The method according to claim 1 , wherein the nickel-poor iron-containing material is the tailings of a nickel ore flotation process.
4. The method according to claim 1 , wherein the dominant form of nickel and other valuable metals in the nickel-poor material is sulphides.
5. The method according to claim 1 , wherein the pulping and leaching solution of the nickel-poor material is sulphuric acid based.
6. The method according to claim 2 , wherein a first part of the iron is precipitated as jarosite.
7. The method according to claim 6 , wherein a second part of the iron dissolved in the leaching solution is precipitated from the solution as hydroxide and goethite by neutralising and oxidising the solution.
8. The method according to claim 1 , wherein the atmospheric leaching is performed in a pH range of 1.3-2.
9. The method according to claim 1 , wherein the atmospheric leaching is performed in a pH range of 2.0-3.0.
10. The method according to claim 2 , wherein a first precipitated part of the iron corresponds to the entire quantity of iron.
11. The method according to claim 2 , wherein the atmospheric leaching is performed in a pH range of 2.0-3.0 and the iron is precipitated as goethite and hydroxide.
12. The method according to claim 2 , wherein a precipitated iron compound is recycled to the leaching stage.
13. The method according to claim 1 , wherein pulping and atmospheric leaching are carried out at a temperature between 60° C. and the boiling point of the solution.
14. The method according to claim 1 , wherein the nickel-poor material is pre-treated before pulping with concentrated sulphuric acid.
15. The method according to claim 1 , wherein the valuable metal sulphides are oxidised to sulphates at elevated oxygen pressure.
16. The method according to claim 2 , wherein the leaching solution formed in sulphide precipitation, from which the valuable metals have been removed, contains magnesium and manganese, which are precipitated from the solution by neutralizing the solution.
17. The method according to claim 1 , wherein the valuable metals of the nickel-poor material in addition to nickel are cobalt, copper and zinc.