Process for preparing a masterbatch in the liquid phase
View Patent ↗The invention relates to a process for the preparation of a masterbatch in the liquid phase based on one or more diene elastomer latexes and on one or more fillers, comprising the following successive stages: preparation of a stable and homogeneous aqueous dispersion by mixing one or more diene elastomer latexes with one or more stable aqueous dispersions of one or more fillers, the said fillers; homogenization of the aqueous dispersion, coagulation within the aqueous dispersion of the said diene elastomer latex or latexes with the filler or fillers by supplying mechanical energy, recovery of the coagulum, drying the recovered coagulum in order to obtain the masterbatch.
1. A process for the preparation of a masterbatch in the liquid phase based on one or more diene elastomer latexes and on one or more fillers, comprising:
preparing a stable and homogeneous aqueous dispersion (C) by mixing
one or more diene elastomer latexes (A) with
one or more stable aqueous dispersions (B) comprising one or more surfactants and one or more fillers,
homogenizing the aqueous dispersion (C),
coagulating within the aqueous dispersion (C) the diene elastomer latex or latexes (A) with the filler or fillers by supplying mechanical energy,
recovering the coagulum,
drying the recovered coagulum in order to obtain the masterbatch.
2. The process according to claim 1 , wherein the recovering the coagulum is carried out by a filtering operation.
3. The process according to claim 1 , wherein the recovering the coagulum is carried out by a centrifuging operation.
4. The process according to claim 1 wherein the diene elastomer latex (A) is a natural rubber latex.
5. The process according to claim 4 , wherein the diene elastomer latex (A) is a concentrated natural rubber latex.
6. The process according to claim 1 , wherein the filler coagulates spontaneously with the said diene elastomer latex or latexes (A).
7. The process according to claim 6 , wherein the filler is carbon black.
8. The process according to claim 6 , wherein the filler is hydrophobized silica.
9. The process according to claim 1 , wherein the surfactant is an anionic surfactant.
10. The process according to claim 9 , wherein the surfactant is sodium dodecyl sulphate.
11. The process according to claim 1 , wherein the concentration of surfactant in the aqueous dispersion (B) is strictly greater than 0.01% by weight, with respect to the total weight of the aqueous dispersion (B).