Rubber composition, production method therefor and tire
Objects of the present invention are to provide a rubber composition that can obtain a rubber elastic body having small rolling resistance and excellent impact resilience and a method for producing the same, and to provide a tire having small rolling resistance and excellent impact resilience. The rubber composition of the present invention is obtained by kneading a conjugated diene polymer (A) having a group with bonding reactivity to silica only at one site of one molecule of the polymer, a polymer (B) having groups with bonding reactivity to silica at a plurality of sites of one molecule of the polymer, and a filler (C) containing silica.
1. A method for producing a rubber composition the method comprising kneading:
a conjugated diene polymer (A) having a group with bonding reactivity to silica only at one site of one molecule of the polymer,
a polymer (B) having groups with bonding reactivity to silica at a plurality of sites of one molecule of the polymer, and
a filler (C) comprising silica.
2. The method of claim 1 , comprising first kneading the conjugated diene polymer (A) and the filler (C) to obtain a kneaded mixture, then kneading the kneaded mixture and the polymer (B).
3. The method of claim 1 , wherein a mass ratio of the conjugated diene polymer (A) to the polymer (B) is in a range from 97/3 to 60/40.
4. The method of claim 1 , wherein the polymer (B) comprises a structural unit derived from a conjugated diene compound.
5. The method of claim 1 , wherein:
the group with bonding reactivity to silica at one site of one molecule of the conjugated diene polymer (A) is at least one functional group selected from the group consisting of a hydrocarbyloxysilyl group, a primary amino group, a secondary amino group, a tertiary amino group, a thiol group, an epoxy group, a thioepoxy group, an oxetane group and a hydrocarbylthio group, and
the groups with bonding reactivity to silica at a plurality of sites of one molecule of the polymer (B) are each independently at least one functional group selected from the group consisting of a hydrocarbyloxysilyl group, a primary amino group, a secondary amino group, a tertiary amino group, a thiol group, an epoxy group, a thioepoxy group, an oxetane group and a hydrocarbylthio group.
6. The method of claim 1 , wherein an amount of silica in the filler (C) is from 10 to 120 parts by mass based on 100 parts by mass of a rubber component comprising the conjugated diene polymer (A) and the polymer (B).
7. A rubber composition obtained by kneading:
a conjugated diene polymer (A) having a group with bonding reactivity to silica only at one site of one molecule of the polymer,
a polymer (B) having groups with bonding reactivity to silica at a plurality of sites of one molecule of the polymer, and
a filler (C) comprising silica.
8. The rubber composition of claim 7 , obtained by first kneading the conjugated diene polymer (A) and the filler (C) to obtain a kneaded mixture, then kneading the kneaded mixture and the polymer (B).
9. The rubber composition of claim 7 , wherein a mass ratio of the conjugated diene polymer (A) to the polymer (B) is in a range from 97/3 to 60/40.
10. The rubber composition of claim 7 , wherein the polymer (B) comprises a structural unit derived from a conjugated diene compound.
11. The rubber composition of claim 7 , wherein:
the group with bonding reactivity to silica at one site of one molecule of the conjugated diene polymer (A) is at least one functional group selected from the group consisting of a hydrocarbyloxysilyl group, a primary amino group, a secondary amino group, a tertiary amino group, a thiol group, an epoxy group, a thioepoxy group, an oxetane group and a hydrocarbylthio group, and
the groups with bonding reactivity to silica at a plurality of sites of one molecule of the polymer (B) are each independently at least one functional group selected from the group consisting of a hydrocarbyloxysilyl group, a primary amino group, a secondary amino group, a tertiary amino group, a thiol group, an epoxy group, a thioepoxy group, an oxetane group and a hydrocarbylthio group.
12. The rubber composition of claim 7 , wherein an amount of silica in the filler (C) is from 10 to 120 parts by mass based on 100 parts by mass of a rubber component comprising the conjugated diene polymer (A) and the polymer (B).
13. A rubber composition comprising:
a rubber component comprising a conjugated diene polymer (A) having a group with bonding reactivity to silica only at one site of one molecule of the polymer and a polymer (B) having groups with bonding reactivity to silica at a plurality of sites of one molecule of the polymer, and
a filler (C) comprising silica.
14. A tire having a tread obtained from the rubber composition of claim 7 .
15. The method of claim 2 , wherein a mass ratio of the conjugated diene polymer (A) to the polymer (B) is in a range from 97/3 to 60/40.
16. The method of claim 2 , wherein the polymer (B) comprises a structural unit derived from a conjugated diene compound.
17. The method of claim 3 , wherein the polymer (B) comprises a structural unit derived from a conjugated diene compound.
18. The method of claim 15 , wherein the polymer (B) comprises a structural unit derived from a conjugated diene compound.
19. The method of claim 2 , wherein:
the group with bonding reactivity to silica at one site of one molecule of the conjugated diene polymer (A) is at least one functional group selected from the group consisting of a hydrocarbyloxysilyl group, a primary amino group, a secondary amino group, a tertiary amino group, a thiol group, an epoxy group, a thioepoxy group, an oxetane group and a hydrocarbylthio group, and
the groups with bonding reactivity to silica at a plurality of sites of one molecule of the polymer (B) are each independently at least one functional group selected from the group consisting of a hydrocarbyloxysilyl group, a primary amino group, a secondary amino group, a tertiary amino group, a thiol group, an epoxy group, a thioepoxy group, an oxetane group and a hydrocarbylthio group.
20. The method of claim 3 , wherein:
the group with bonding reactivity to silica at one site of one molecule of the conjugated diene polymer (A) is at least one functional group selected from the group consisting of a hydrocarbyloxysilyl group, a primary amino group, a secondary amino group, a tertiary amino group, a thiol group, an epoxy group, a thioepoxy group, an oxetane group and a hydrocarbylthio group, and
the groups with bonding reactivity to silica at a plurality of sites of one molecule of the polymer (B) are each independently at least one functional group selected from the group consisting of a hydrocarbyloxysilyl group, a primary amino group, a secondary amino group, a tertiary amino group, a thiol group, an epoxy group, a thioepoxy group, an oxetane group and a hydrocarbylthio group.