Alkali niobate-based piezoelectric material and a method for making the same
View Patent ↗An alkali niobate-based piezoelectric material having the general formula {(K 1-a Na a ) 1-b Li b }(Nb 1-c-d Ta c Sb d )O 3 +x mol % Ba n TiO 3 +y mol % CuO, where 0≦a≦0.9, 0≦b≦0.3, 0<c≦0.5, 0≦d≦0.1, 0.5≦x<10.0, 0.1≦y≦8.0, and 0.9≦n≦1.2.
1. A method for making an alkali niobate-based piezoelectric material having the general formula {(K 1-a Na a ) 1-b Li b }(Nb 1-c-d Ta c Sb d )O 3 +x mol % Ba n TiO 3 +y mol % CuO where 0.35<a<0.65, 0.03≦b≦0.15, 0.05≦c≦0.25, 0≦d≦0.01 or 0.03≦d≦0.06, 2.0≦x≦4.0, 1.0≦y≦3.0, and 0.95≦n≦1.05,
and having characteristics of: an electromechanical coupling coefficient Kp≧25%,
a relative dielectric constant εr≧800, and
a mechanical quality factor Qm≧800,
the method comprising:
mixing a solvent and a raw material of a compound that is the piezoelectric material;
primary-heating a mixture of the solvent and the raw material of the compound, at a temperature lower than a sintering temperature;
forming into a certain shape the primary-heated mixture in which a binder is added; and
heating the shaped product to sinter in an atmosphere consisting of oxygen.
2. The method for making an alkali niobate-based piezoelectric material according claim 1 , wherein
the piezoelectric material contains a compound having the general formula K z Na (1-z) NbO 3 , wherein 0.02≦z≦0.5.