PCC filler composition for improved printability of supercalendered papers
View Patent ↗A method of blending a fine precipitated calcium carbonate (PCC) filler with larger PCC, the resulting blend to be used alone or in conjunction with a ground carbonate, clay or other filler, resulting in improved porosity by the lowering of the porosity of supercalendered paper, thereby imparting improved and offset printability. The fine PCC can be ultrafine PCC filler which then is blended with other fillers including but not limited to pigments. These fillers which are blended with the fine PCC include commercial and experimental PCC and commercial clays. Ultrafine PCC has agglomerates of small, discrete particles. Ultrafine PCC for use in the invention has a specific surface area of about 20 m2/g as measured by BET gas adsorption. As measured by a sedigraph, the average size of these agglomerates is from 0.4 to 1.1 microns.
1. A pigment composition comprising:
a) first precipitated calcium carbonate pigment comprising PCC particles; and
b) a fine precipitated calcium carbonate having an average size range of 0.06 to 1.1 microns, a particle size distribution D 20 of about 0.2 microns or less, and a specific surface area of at least about 20 m 2 /g;
wherein the weight ratio of the first precipitated calcium carbonate pigment to the fine precipitated calcium carbonate is about 60:40 to 75:25.
2. The pigment composition of claim 1 wherein the fine precipitated calcium carbonate has a specific surface area between about 20 m 2 /g to 50 m 2 /g.
3. The pigment composition of claim 1 wherein the fine precipitated calcium carbonate has a PCC particle size distribution D 90 of about 1.0 microns or less.
4. The pigment composition of claim 1 wherein the fine precipitated calcium carbonate has a PCC particle size distribution D 90 of about 1.5 microns or less.
5. The pigment composition of claim 1 wherein the fine precipitated calcium carbonate has a PCC particle size distribution D 90 of about 2.0 microns or less.
6. The pigment composition of claim 1 wherein the fine precipitated calcium carbonate has a PCC particle size distribution D 50 of about 0.4 microns or less.
7. The pigment composition of claim 1 wherein the fine precipitated calcium carbonate has a PCC particle size distribution D 50 of about 0.8 microns or less.
8. The pigment composition of claim 1 wherein the first precipitated calcium carbonate pigment PCC particles are non-platy PCC particles.
9. The pigment composition of claim 1 wherein the first precipitated calcium carbonate pigment PCC particles have a specific surface area of at least about 10 m 2 /g or greater.
10. The pigment composition of claim 1 wherein the first precipitated calcium carbonate pigment PCC particles have a PCC particle size distribution D 90 of about 3.0 microns or less.
11. A pigment composition comprising:
a) first precipitated calcium carbonate pigment comprising PCC particles; and
b) a fine precipitated calcium carbonate having an average size range of 0.06 to 1.1 microns, a particle size distribution D 20 of about 2.0 microns or less, and a specific surface area of at least about 20 m 2 /g;
wherein the weight ratio of the first precipitated calcium carbonate pigment to the fine precipitated calcium carbonate is about 60:40.