Duplex stainless steel
View Patent ↗A duplex stainless steel containing, by mass %: C: not more than 0.03%, Si: not more than 0.3%, Mn: not more than 3.0%, P: not more than 0.040%, S: not more than 0.008%, Cu: 0.2 to 2.0%, Ni: 5.0 to 6.5%, Cr: 23.0 to 27.0%, Mo: 2.5 to 3.5%, W: 1.5 to 4.0%, and N: 0.24 to 0.40%, the balance being Fe and impurities, wherein a σ phase susceptibility index X (=2.2Si+0.5Cu+2.0Ni+Cr+4.2Mo+0.2W) is not more than 52.0; a strength index Y (=Cr+1.5Mo+10N+3.5W) is not less than 40.5; and a pitting resistance equivalent PREW (=Cr+3.3(Mo+0.5W)+16N) is not less than 40. This duplex stainless steel is excellent in corrosion resistance and embrittlement cracking resistance.
1. A duplex stainless steel having a chemical composition consisting of, by mass %:
C: not more than 0.03%, Si: not more than 0.3%, Mn: not more than 3.0%, P: not more than 0.040%, S: not more than 0.008%, Cu: 0.2 to 2.0%, Ni: 5.0 to 6.5%, Cr: 23.0 to 27.0%, Mo: 2.5 to 3.5%, W: 1.5 to 4.0%, and N: 0.24 to 0.40%, the balance being Fe and impurities,
wherein a σ phase susceptibility index X represented by the following Formula (1) is not more than 52.0;
a strength index Y represented by the following Formula (2) is not less than 40.5; and
a pitting resistance equivalent PREW represented by the following Formula (3) is not less than 40:
X=2.2Si+0.5Cu+2.0Ni+Cr+4.2Mo+0.2W (1)
Y=Cr+1.5Mo+10N+3.5W (2)
PREW=Cr+3.3(Mo+0.5W)+16N (3)
where a symbol of each element in the Formulas (1), (2), and (3) denotes a content (mass %) of the element,
wherein an impact value regulated by JIS Z 2242 (2005) after aging at 900° C. and 600 seconds is not less than 18 J/cm 2 and a 0.2% yield stress after solution heat treatment obtained by a tensile test using No. 10 test specimen of JIS Z 2201 (1998) is not less than 620 MPa.
2. A duplex stainless steel having a chemical composition consisting of, by mass %,
C: not more than 0.03%, Si: not more than 0.3%, Mn: not more than 3.0%, P: not more than 0.040%, S: not more than 0.008%, Cu: 0.2 to 2.0%, Ni: 5.0 to 6.5%, Cr: 23.0 to 27.0%, Mo: 2.5 to 3.5%, W: 1.5 to 4.0%, N: 0.24 to 0.40%, and one or more elements selected from among Ca: not more than 0.02%, Mg: not more than 0.02%, and B: not more than 0.02%, the balance being Fe and impurities,
wherein a σ phase susceptibility index X represented by the following Formula (1) is not more than 52.0;
a strength index Y represented by the following Formula (2) is not less than 40.5; and
a pitting resistance equivalent PREW represented by the following Formula (3) is not less than 40:
X=2.2Si+0.5Cu+2.0Ni+Cr+4.2Mo+0.2W (1)
Y=Cr+1.5Mo+10N+3.5W (2)
PREW=Cr+3.3(Mo+0.5W)+16N (3)
where a symbol of each element in the Formulas (1), (2), and (3) denotes a content (mass %) of the element,
wherein an impact value regulated by JIS Z 2242 (2005) after aging at 900° C. and 600 seconds is not less than 18 J/cm 2 and a 0.2% yield stress after solution heat treatment obtained by a tensile test using No. 10 test specimen of JIS Z 2201 (1998) is not less than 620 MPa.