Film formation composition for preventing blackening of steel sheet, and steel sheet having film formed by composition
View Patent ↗Provided is a film formation composition for improving the blackening of the surface of a steel sheet, particularly, the surface of a steel sheet containing Mg on the surface thereof, such as a Mg sheet, a plated steel sheet having a plated layer comprising Mg, and the like, a steel sheet comprising a film formed by the composition, and a method for forming the film. Provided are a film formation composition for preventing the blackening of the surface of the steel sheet, comprising: 2.5-7.5 parts by weight of a water-soluble phenoxy resin; 0.1-0.5 parts by weight of a fluorometal acid; 0.1-0.5 parts by weight of a metal compound; and 1-5 parts by weight of a cross-linking agent.
1. A composition for forming a blackening resistance film on a steel sheet containing magnesium, the composition comprising:
3.75 to 7.5 parts by solid weight of a water-soluble phenoxy resin, wherein the water-soluble phenoxy resin has a number average molecular weight of 20,000 to 60,000;
0.1 to 0.5 parts by solid weight of a metallic compound, wherein the metallic compound comprises a salt, oxide, or colloid and is eluted to form an insoluble oxide film; and 1 to 5 parts by solid weight of a crosslinking agent.
2. The composition of claim 1 , wherein the fluorometallic acid comprises at least one selected from the group consisting of hexafluorotitanic acid, hexafluorosilicic acid, hexafluorozirconic acid, hexafluorotungstic acid, hexafluoromolybdic acid, and hexalluorogermanic acid.
3. The composition of claim 1 , wherein the metallic compound comprises at least one of silicon, aluminum, manganese, titanium, cerium, zinc, molybdenum, vanadium, zirconium, and combinations thereof.
4. The composition of claim 3 , wherein the metallic compound exists in water as a salt and/or a nano-sized colloid.
5. The composition of claim 1 , wherein the crosslinking agent comprises at least one selected from the group consisting of 3-glycidoxypropyltrimethoxysilane, 2-(3/4-epoxycyclohexyl)ethyltrimethoxysilane, 2-(3,4-epoxycyclohexyl)ethyltriethoxysilane, and 3-glycidoxypropylmethyldiethoxysilane.
6. A steel sheet comprises:
magnesium on at least a surface thereof; and
a blackening resistance film formed by the composition of claim 1 .
7. The steel sheet of claim 6 , wherein the blackening resistance film is formed on the surface of the steel sheet containing magnesium and has a dry density of 100 mg/m 2 to 1000 mg/m 2 .
8. The steel sheet of claim 6 , wherein the steel sheet is a magnesium steel sheet, a magnesium-plated steel sheet, or a magnesium-alloy-plated steel sheet.
9. The steel sheet of claim 8 , wherein the magnesium-alloy-plated steel sheet comprises a magnesium alloy plating layer selected from the group consisting of Zn—Al—Mg, Zn—Al—Mg—Si, Zn—Mg, Mg—Zn, Al—Mg, and Al—Mg—Si.
10. The steel sheet of claim 6 , wherein the fluorometallic acid comprises at least one selected from the group consisting of hexafluorotitanic acid, hexafluorosilicic acid, hexafluorozirconic acid, hexafluorotungstic acid, hexafluoromolybdic acid, and hexafluorogermanic acid.
11. The steel sheet claim 6 , wherein the metallic compound comprises at least one of silicon, aluminum, manganese, titanium, cerium, zinc, molybdenum, vanadium, zirconium, and combinations thereof.
12. The steel sheet of claim 6 , wherein the metallic compound exists in water as a salt and/or a nano-sized colloid.
13. The steel sheet of claim 6 , wherein the crosslinking agent comprises at least one selected from the group consisting of 3-glycidoxypropyltrimethoxysilane, 2-(3 ,4-epoxycyclohexyl)ethyltrimethoxysilane, 2-(3 ,4-epoxycyclohexyl) ethyltriethoxysilane, and 3 -glycidoxypropylmethyldiethoxysilane.