Reverse osmosis membrane including nano-silver wire layer and fabrication method thereof
There are provided a reverse osmosis membrane comprising a porous support; a silver nanowire layer formed on the porous support; and a polyamide film formed on the silver nanowire layer, and a fabrication method of a reverse osmosis membrane, the method comprising coating a porous support with an aqueous amine solution including silver nanowires to form a silver nanowire layer; and bringing the silver nanowire layer into contact with an aliphatic hydrocarbide-based organic solution including acyl halide to form a polyamide film.
1. A reverse osmosis membrane comprising:
a porous support;
a silver nanowire layer formed on the porous support; and
a polyamide film formed on the silver nanowire layer.
2. The reverse osmosis membrane of claim 1 , wherein the silver nanowire layer has a thickness equal to 1% to 50% of the polyamide film.
3. The reverse osmosis membrane of claim 1 , wherein the porous support is formed by coating non-woven fabric with one or more compounds selected from the group consisting of polysulfone, polyethersulfone, polycarbonate, polyethyleneoxide, polyimide, polyetherimide, polyetheretherketone, polypropylene, polymethylpentene, polymethylchloride, and polyvinylidene fluoride.
4. The reverse osmosis membrane of claim 1 , wherein the polyamide film is formed through interfacial polymerization between an amine compound and an acyl halide compound.
5. The reverse osmosis membrane of claim 4 , wherein the amine compound is one or more compounds selected from the group consisting of m-phenylenediamine, p-phenylenediamine, 1,3,6-benzenetriamine, 4-chloro-1,3-phenylenediamine, 6-chloro-1,3-phenylenediamine, 3-chloro-1,4-phenylenediamine, and any mixture thereof.
6. The reverse osmosis membrane of claim 4 , wherein the acyl halide compound is one or more compounds selected from the group consisting of trimesoylchloride, isophthaloylchloride, and terephthaloylchloride.
7. The reverse osmosis membrane of claim 1 , wherein the reverse osmosis membrane has an initial salt rejection coefficient equal to or greater than 98% and an initial permeate flow rate equal to or greater than 44 gallon/ft 2 ·day, having excellent chlorine-resistance and anti-contamination properties.
8. The reverse osmosis membrane claim 1 , wherein the reverse osmosis membrane has a salt rejection coefficient equal to or greater than 96% and a permeate flow rate equal to or greater than 36 gallon/ft 2 ·day when two hours have elapsed after the injection of casein.
9. The reverse osmosis membrane of claim 1 , wherein the reverse osmosis membrane has a salt rejection coefficient equal to or greater than 90% and a permeate flow rate equal to or greater than 40 gallon/ft 2 ·day when twelve hours have elapsed after the injection of an NaOCl aqueous solution of 2,000 ppm.
10. A fabrication method of a reverse osmosis membrane, the method comprising:
coating a porous support with an aqueous amine solution including silver nanowires to form a silver nanowire layer; and
bringing the silver nanowire layer into contact with an aliphatic hydrocarbide-based organic solution including acyl halide to form a polyamide film.
11. The fabrication method of claim 10 , wherein the aqueous amine solution contains the silver nanowires in the amount of 0.001 wt % to 0.5 wt %.