High-strength austenitic stainless steel for high-pressure hydrogen gas
View Patent ↗There is provided an austenitic stainless steel for high-pressure hydrogen gas consisting, by mass percent, of C: 0.10% or less, Si: 1.0% or less, Mn: 3% or more to less than 7%, Cr: 15 to 30%, Ni: 10% or more to less than 17%, Al: 0.10% or less, N: 0.10 to 0.50%, and at least one kind of V: 0.01 to 1.0% and Nb: 0.01 to 0.50%, the balance being Fe and impurities, wherein in the impurities, the P content is 0.050% or less and the S content is 0.050% or less, the tensile strength is 800 MPa or higher, the grain size number (ASTM E112) is No. 8 or higher, and alloy carbo-nitrides having a maximum diameter of 50 to 1000 nm are contained in the number of 0.4/μm 2 or larger in cross section observation.
1. An austenitic stainless steel for hydrogen gas comprising: by mass percent, C: 0.10% or less, Si: 1.0% or less, Mn: 3% or more to less than 7%, Cr: 15 to 24%, Ni: 10% to 15%, Al: 0.001 to 0.10%, N: 0.10 to 0.50%, and V: 0.01 to 1.0%, the balance being Fe and impurities,
wherein in the impurities, the P content is 0.050% or less and the S content is 0.050% or less, the tensile strength is 800 MPa or higher, a relative rupture elongation is 80% or more, the grain size number in accordance with ASTM E112 is No. 8 or higher, and alloy carbo-nitrides having a maximum diameter of 50 to 1000 nm are contained in the number of 0.4/μm 2 or larger in cross section observation.
2. The austenitic stainless steel for hydrogen gas according to claim 1
wherein the austenitic stainless steel is subjected to solid solution heat treatment at a temperature of 1000 to 1200° C., next being subjected to cold rolling in which the reduction of area is 20% or more, and thereafter is again subjected to heat treatment in the temperature range of 900° C. or higher and lower than the solution treatment temperature.
3. An austenitic stainless steel for hydrogen gas comprising: by mass percent, C: 0.10% or less, Si: 1.0% or less, Mn: 3% or more to less than 7%, Cr: 15 to 24%, Ni: 10% to 15%, Al: 0.001 to 0.10%, N: 0.10 to 0.50%, and V: 0.010 to 1.0%, further containing Nb: 0.01 to 0.50%, and/or containing at least one element selected from element groups of a first group to a fourth group described below, the balance being Fe and impurities,
wherein in the impurities, the P content is 0.050% or less and the S content is 0.050% or less, the tensile strength is 800 MPa or higher, a relative rupture elongation is 80% or more, the grain size number in accordance with ASTM E112 is No. 8 or higher, and alloy carbo-nitrides having a maximum diameter of 50 to 1000 nm are contained in the number of 0.4/μm 2 or larger in cross section observation:
first group elements: Mo: 0.3 to 3.0% and W: 0.3 to 6.0%;
second group elements: Ti: 0.001 to 0.5%, Zr: 0.001 to 0.5%, Hf: 0.001 to 0.3%, and Ta: 0.001 to 0.6%;
third group elements: B: 0.0001 to 0.020%, Cu: 0.3 to 5.0%, and Co: 0.3 to 10.0%; and
fourth group elements: Mg: 0.0001 to 0.0050%, Ca: 0.0001 to 0.0050%, La: 0.0001 to 0.20%, Ce: 0.0001 to 0.20%, Y: 0.0001 to 0.40%, Sm: 0.0001 to 0.40%, Pr: 0.0001 to 0.40%, and Nd: 0.0001 to 0.50%.
4. The austenitic stainless steel for hydrogen gas according to claim 2 , wherein the austenitic stainless steel is subjected to solid solution heat treatment at a temperature of 1000 to 1200° C., next being subjected to cold rolling in which the reduction of area is 20% or more, and thereafter is again subjected to heat treatment in the temperature range of 900° C. or higher and lower than the solution treatment temperature.