Hot stamped high strength part excellent in post painting anticorrosion property and method of production of same

1. A hot stamped high strength part formed of a steel sheet which is excellent in post painting anticorrosion property, comprising an alloy plating layer comprising an Al—Fe intermetallic compound phase on the surface of the steel sheet,

said alloy plating layer is comprised from phases of a plurality of intermetallic compounds,

a mean linear intercept length of crystal grains of a phase containing Al: 40 to 65 mass % among said phases of the plurality of intermetallic compounds is 3 to 20 μm,

an average value of thickness of said Al—Fe alloy plating layer is 10 to 50 μm, and

a ratio of the average value of thickness to the standard deviation of thickness of said Al—Fe alloy plating layer satisfies the following relationship:

0<standard deviation of thickness/average value of thickness≦0.15.

2. The hot stamped high strength part which is excellent in post painting anticorrosion property as set forth in claim 1 characterized in that said ratio of the average value of thickness to the standard deviation of thickness is 0.1 or less.

3. The hot stamped high strength part which is excellent in post painting anticorrosion property as set forth in claim 1 or 2 characterized in that said Al—Fe alloy plating layer contains, by mass %, Si: 2 to 7%.

4. The hot stamped high strength part which is excellent in post painting anticorrosion property as set forth in claim 1 or 2 characterized in that a surface film layer which contains ZnO is laid on the surface of said Al—Fe alloy plating layer.

5. The hot stamped high strength part which is excellent in post painting anticorrosion property as set forth in claim 4 characterized in that a content of ZnO of said surface film layer is, converted to mass of Zn, 0.3 to 7 g/m 2 per side.

6. The hot stamped high strength part which is excellent in post painting anticorrosion property as set forth in claim 1 or 2 characterized in that said steel sheet is comprised of a steel sheet of chemical ingredients which comprise as ingredients, by mass %,

C: 0.1 to 0.5%,

Si: 0.01 to 0.7%,

Mn: 0.2 to 2.5%,

Al: 0.01 to 0.5%,

P: 0.001 to 0.1%,

S: 0.001 to 0.1%,

N: 0.0010% to 0.05%, and

a balance of Fe and unavoidable impurities.

7. The hot stamped high strength part which is excellent in post painting anticorrosion property as set forth in claim 6 characterized in that said steel sheet further comprises, by mass %, one or more elements selected from

Cr: over 0.4 to 3%,

Mo: 0.005 to 0.5%,

B: 0.0001 to 0.01%,

W: 0.01 to 3%,

V: 0.01 to 2%,

Ti: 0.005 to 0.5%,

Nb: 0.01 to 1%

Ni: 0.01 to 5%,

Cu: 0.1 to 3%,

Sn: 0.005% to 0.1%, and

Sb: 0.005% to 0.1%.